Physical Properties | Metric | English | Comments |
---|---|---|---|
Particle Size | 8.0 µm | 8.0 µm | median; Microtrac |
Nyco 400 WOLLASTOCOAT® Wollastonite This grade is recommended for polymer reinforcement.Wollastonite is a naturally occurring white mineral with an acicular (needle-shaped) particle structure. This distinctive particle morphology make.. |
|||
Particle Size | 8.0 µm | 8.0 µm | median; Microtrac |
Nyco NYAD® 400 Wollastonite Chemically treated powdered grade.Wollastonite is a naturally occurring white mineral with an acicular (needle-shaped) particle structure. This distinctive particle morphology makes wollastonite an .. |
|||
Particle Size | 8.0 µm | 8.0 µm | Median Grain Diameter |
Nabaltec APYRAL® 24 Al(OH)3 APYRAL ® from Nabaltec is an environmentally friendly halogen free product which is used as a flame retardant filler in a wide variety of rubber and polymeric materials. During thermal decompositio.. |
|||
Particle Size | 8.0 µm | 8.0 µm | 50% finer than |
Potters Industries Sphericel® 110P8 Hollow Glass Spheres Description: Sphericel® 110P8 hollow glass spheres displace the same volume of resin as solid spheres of the same size, but are lighter. Using Sphericel® hollow glass spheres, plastics engineers c.. |
|||
Particle Size | 8.0 µm | 8.0 µm | mean |
Imerys Minsparâ„¢ 4 Ground Feldspar Minsparâ„¢ 4 is a medium particle size, ground Feldspar with a tightly controlled particle size distribution. The small amount of material retained on a 325 mesh screen, in conjunction with excel.. |
|||
Particle Size | 8.0 - 12 µm | 8.0 - 12 µm | 50% |
H.C. Starck Amperit® 140.067 Tungsten (W) HS Number: 81011000 |
|||
Particle Size | 8.0 - 12 µm | 8.0 - 12 µm | 10% |
H.C. Starck Amperit® 519.059 Agglomerated, Sintered Tungsten Carbide-Cobalt 88-12 (WC-CO) |
|||
Particle Size | 8.0 - 12 µm | 8.0 - 12 µm | 10% |
H.C. Starck Amperit® 558.059 Tungsten Carbide-Cobalt-Chromium 86-10-4 (WC-Co-Cr) |
|||
Particle Size | 8.0 µm | 8.0 µm | Average Particle Size/Laser Diffraction D50 |
H.C. Starck Grade A Lanthanum Hexaboride, LaB6 Powder for cathodes. |
|||
Particle Size | <= 8.0 µm | <= 8.0 µm | 90% less than |
H.C. Starck Grade AT Yttrium Oxide Sintering additive for Si3N4 and ALNStabilizer for zirconias (PSZ) and insulating coatings (TBC`s)Catalyst carrierYttria stabilized zirconias electrolytes for solid oxide fuel cellsLuminescent mater.. |
|||
Particle Size | <= 8.0 µm | <= 8.0 µm | 90% less than |
H.C. Starck Grade B Zirconium Carbide, ZrC Additive for hard metalsAdditive for powder metallurgyModerator in solid fuel propellant |
|||
Particle Size | <= 8.0 µm | <= 8.0 µm | 3rd Streak; Fineness of Grind |
Gwent Electronic Materials C2031105D2 Palladium Ink Palladium Ink C2031105D2 is an ink formulated for screen printing for use on Fuel Cells. It is suitable for application onto Solid Oxide Fuel Cells.The ink has been made at a ready to use viscosity.. |
|||
Particle Size | <= 8.0 µm | <= 8.0 µm | 23% |
SGL Carbon Group CF 1135 Carbon Filler Good mechanical strength, good sliding properties, high temperature resistance, high thermal shock resistance, low wettability, high corrosion resistance, high thermal conductivity, high purity, and.. |
|||
Particle Size | <= 8.0 µm | <= 8.0 µm | 13% |
SGL Carbon Group CF 480 Graphite Filler Good mechanical strength, good sliding properties, high temperature resistance, high thermal shock resistance, low wettability, high corrosion resistance, high thermal conductivity, high purity, and.. |
|||
Particle Size | <= 8.0 µm | <= 8.0 µm | 28% |
SGL Carbon Group CF 5250 Carbon Filler Good mechanical strength, good sliding properties, high temperature resistance, high thermal shock resistance, low wettability, high corrosion resistance, high thermal conductivity, high purity, and.. |
|||
Particle Size | 8.0 µm | 8.0 µm | |
Silberline "A" Series A-2291FG A-2291FG is an ultra fine, high opacity, non-leafing aluminum pigment for solvent based general industrial coatings. Due to the small particle size, this grade is well suited for imparting high opac.. |
|||
Particle Size | 8.0 µm | 8.0 µm | Before Conversion |
Silberline Silvet® 330-20-E Silvet® E grades are economical aluminum pigments provided in pellet form for easy handling and incorporation. They are composed of 80% aluminum pigment and 20% polyolefin and are compatible with.. |
|||
Particle Size | 8.0 µm | 8.0 µm | |
Silberline SparkleBriteâ„¢ 320NL-PA SparkleBriteâ„¢ pigments are non-leafing aluminum pigment pastes carried in isopropyl alcohol. These grades are based on cornflake geometry and produce strong metallic effects in solvent and wate.. |
|||
Particle Size | 8.0 - 12 µm | 8.0 - 12 µm | d90, Guaranteed |
TIMCAL TIMREX® C-LUB 304 Primary Synthetic Graphite Information provided by TIMCAL |
|||
Particle Size | 8.0 µm | 8.0 µm | d50 |
TIMCAL TIMREX® KS15 Primary Synthetic Graphite TIMREX Primary Synthetic Graphite is produced in a unique highly controlled graphitization process which assures narrow specifications and unequalled consistent quality due to: monitoring of all pro.. |
|||
Particle Size | 8.0 - 17 µm | 8.0 - 17 µm | For Median |
CIMBAR Crescent 12 Calcium Carbonate (CaCO3), Fine Powder CIMBAR's Crescent product line is a natural calcium carbonate ground to various particle size distributions. The crystalline structure of the calcium carbonate in Crescent products has a predominan.. |
|||
Particle Size | <= 8.0 µm | <= 8.0 µm | Max |
CIMBAR Miti-Wite B1 Chemically Purified White Barite (BaSO4) Miti-Wite barite products are produced using a proprietary chemical process to enhance the purity of the natural barium sulfate ore. Miti-Wite products are available in a variety of particle sizes .. |
|||
Particle Size | 8.0 µm | 8.0 µm | @ 90% |
CIMBAR MV 603 Talc MV Series talcs are produced from high purity talc ore, which provide good color, acid resistance and excellent barrier properties when used in paint & coating formulations. MV Series talcs are pla.. |
|||
Particle Size | 8.0 - 25 µm | 8.0 - 25 µm | fiber diameter |
BCC Products BC 32 Fibrous Glass BC 32, microglass milled fibers will increase the mechanical strengths, such as impact strength, tensile strength, compressive strength, and flexural strength in plastic tooling compounds. They are .. |
|||
Particle Size | 8.0 µm | 8.0 µm | average; ISO 13321 |
3M Dyneon™ TF 9205 PTFE 3M™ Dyneon™ PTFE TF micropowders can be used as additives in many different applications and at concentrations typically from 5 to 20%. Homogeneous incorporation helps ensure optimum performance. .. |
|||
Particle Size | 8.0 - 14 µm | 8.0 - 14 µm | average |
Momentive Performance Materials PolarTherm® PT140 Boron Nitride (BN) Powder Fine Hexagonal BN PowderWhen used in a variety of polymeric materials, PolarTherm™'s heat dissipating capability helps extend the service life and enhance the reliability of electronic componen.. |
|||
Particle Size | 8.0 µm | 8.0 µm | Average Diameter |
Potters Industries Conduct-O-Fil® SN08P40 Silver-coated Sub-10 micron Particles Conduct-O-Fil® conductive particles are engineered to meet a broad range of conductive and electro magnetic interference requirements. A variety of particle shapes offers the formulator additional .. |
|||
Particle Size | 8.0 - 12 µm | 8.0 - 12 µm | 10% |
H.C. Starck Amperit® 526.059 Agglomerated, Sintered Tungsten Carbide-Cobalt (WC-Co) 83-17 |
|||
Particle Size | 8.0 - 12 µm | 8.0 - 12 µm | 10% |
H.C. Starck Amperit® 547.002 Tungsten Carbide-Nickel 88-12 (WC-Ni) |
|||
Particle Size | 8.0 - 12 µm | 8.0 - 12 µm | 10% |
H.C. Starck Amperit® 551.059 Tungsten Carbide - Chromium Carbide - Nickel 70-20-7 (W-CrC-Ni) |