Polymer Property : Particle Size = 5.0 µm Product List
Physical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Particle Size | >= 5.0 µm | >= 5.0 µm | 10% smaller than |
| Nyco NYGLOS® 12 Wollastonite High aspect ratio grade. This grade is recommended for polymer reinforcement.Wollastonite is a naturally occurring white mineral with an acicular (needle-shaped) particle structure. This distinctiv.. |
|||
| Particle Size | <= 5.0 µm | <= 5.0 µm | 84% of particles less than |
| Old Hickory S-4 Tennessee Ball Clay The S-4 clay is designed for all types of casting formulas ranging from low fire earthenware to vitreous compositions. It has excellent response to deflocculation and very good casting rate while ma.. |
|||
| Particle Size | 5.0 µm | 5.0 µm | Average Diameter |
| Potters Industries Conduct-O-Fil® SG05TF40 Silver-coated Sub-10 micron Particles Conduct-O-Fil® conductive particles are engineered to meet a broad range of conductive and electro magnetic interference requirements. A variety of particle shapes offers the formulator additional .. |
|||
| Particle Size | 5.0 - 100 µm | 5.0 - 100 µm | range |
| Potters Industries Q-Cel® 6048 Performance Benefits: A low-density, performance-enhancing additive.Fewer defects: excellent mold flow, uniform dispersionReduced compound density and viscosityIncreased acoustic and thermal insulat.. |
|||
| Particle Size | 5.0 - 135 µm | 5.0 - 135 µm | |
| Potters Industries Q-Cel® 7023S Hollow Engineered Glass Microspheres Q-CEL® hollow glass microspheres are alternatives to conventional fillers and additives such as silicas, calcium carbonates, talc, clay, etc. A variety of particle sizes, densities and strengths me.. |
|||
| Particle Size | <= 5.0 µm | <= 5.0 µm | |
| PolyOne Aquamix™ 142 Latex Storage Stability: In excess of 6 months when stored under proper conditions in original sealed container. Keep from freezing. Water lost by evaporation can adversely affect viscosity, dispersabilit.. |
|||
| Particle Size | 5.0 µm | 5.0 µm | |
| Poco Graphite AXF-5Q Industrial Grade Graphite POCO’s specialty graphite materials are used in a wide range of highly technical and industrial applications. Each grade has characteristics and properties that allow the user to match the ideal gr.. |
|||
| Particle Size | 5.0 µm | 5.0 µm | mean aggregate size |
| NanoScale NanoActive® Aluminum Oxide Plus NanoActive Al2O3 Plus is produced using proprietary processes to obtain high specific surface area, high porosity (75% are mesopores), low density, weakly aggregated material possessing high adsorpt.. |
|||
| Particle Size | 5.0 - 50 µm | 5.0 - 50 µm | Spherical shape, 5-50 micron distribution. ETM = Equistar Test Method; ETM Malvern |
| LyondellBasell Microthene® F FN51000 Low Density Polyethylene General DescriptionMicrothene F polyolefin powders are ultra-fine, spherically shaped particles with narrow size distribution suitable for use in a broad range of specialty applications. Microthene.. |
|||
| Particle Size | 5.0 µm | 5.0 µm | 50% of particles |
| Ferro EG 2778 Thick Film Glass Glass Type: Si-Al-Ca Typical Powder Form: MVG Typical Application: Dielectric Ferro produces standard and custom glass products that are used in thick film compositions including resistors, conduct.. |
|||
| Particle Size | 5.0 µm | 5.0 µm | 50% of particles |
| Ferro EG 2783 Thick Film Glass Glass Type: Pb-B Typical Powder Form: MVG Typical Application: Die Attachment Ferro produces standard and custom glass products that are used in thick film compositions including resistors, conduct.. |
|||
| Particle Size | 5.0 - 10 µm | 5.0 - 10 µm | d50 |
| Magyar Aluminum ALO-DN-7P Alumina Ground Alumina |
|||
| Particle Size | 5.0 - 10 µm | 5.0 - 10 µm | d50 |
| Magyar Aluminum ALO-P95-08 Alumina Alumina for Polishing |
|||
| Particle Size | 5.0 µm | 5.0 µm | 98% finer than |
| Imerys Aftonâ„¢ R Kaolin Afton is a fine-grained kaolin used asa a filler in hard rubber products, plastic products, adhesives, protective coatings and similar applications.Information provided by Imerys |
|||
| Particle Size | 5.0 µm | 5.0 µm | 82% finer than |
| Imerys Allenâ„¢ Kaolin Allen is an intermediate-grained kaolin suitable for use as a filler and pigment in a wide variety of industrial applications such as soft rubber, plastics, ceiling tile, adhesives and paper product.. |
|||
| Particle Size | 5.0 µm | 5.0 µm | 81.5% finer than |
| Imerys DB-Floatâ„¢ Kaolin Information provided by Imerys |
|||
| Particle Size | 5.0 µm | 5.0 µm | 75% finer than |
| Imerys KT Castâ„¢ Kaolin KT Cast is a coarse-grained, white firing kaolin that is used primarily in casting bodies based on its fast casting and exceptional deflocculation characteristics.Information provided by Imerys |
|||
| Particle Size | 5.0 µm | 5.0 µm | 81% finer than |
| Imerys KT-Cast/Rogersâ„¢ Kaolin Information provided by Imerys |
|||
| Particle Size | 5.0 µm | 5.0 µm | 50% of particles |
| Ferro EG 2791 Thick Film Glass Glass Type: Bi-Pb-Zn Typical Powder Form: MVG Typical Application: End Termination Ferro produces standard and custom glass products that are used in thick film compositions including resistors, co.. |
|||
| Particle Size | <= 5.0 µm | <= 5.0 µm | Main Break; Fineness of Grind |
| Gwent Electronic Materials C2031105D2 Palladium Ink Palladium Ink C2031105D2 is an ink formulated for screen printing for use on Fuel Cells. It is suitable for application onto Solid Oxide Fuel Cells.The ink has been made at a ready to use viscosity.. |
|||
| Particle Size | 5.0 µm | 5.0 µm | Mean Value, Laser diffraction; QSOP-5&75 |
| Shamrock Technologies MicroFLON® 1253 Thermoplastic Grade PTFE Additive Special grade for fine dispersion.The addition of micronized polytetrafluoroethylene (PTFE) powder to polymeric resins provides greatly increased resistance to surface wear and abrasion. PTFE has a.. |
|||
| Particle Size | 5.0 µm | 5.0 µm | |
| Shin-Etsu Silicones KSP-100 Fluid Information Provided by Shin-Etsu Silicones of America, Inc. |
|||
| Particle Size | 5.0 µm | 5.0 µm | Springback 11.5%, pressure 0.477 t/cc |
| TIMCAL TIMREX® KS5-44 Primary Synthetic Graphite TIMREX Primary Synthetic Graphite is produced in a unique highly controlled graphitization process which assures narrow specifications and unequalled consistent quality due to: monitoring of all pro.. |
|||
| Particle Size | 5.0 µm | 5.0 µm | Springback 11.5%, pressure 0.477 t/cc |
| TIMCAL TIMREX® KS75 Primary Synthetic Graphite TIMREX Primary Synthetic Graphite is produced in a unique highly controlled graphitization process which assures narrow specifications and unequalled consistent quality due to: monitoring of all pro.. |
|||
| Particle Size | 5.0 - 500 µm | 5.0 - 500 µm | |
| Trelleborg Fillite® SG (500) Alumino-silicate Cenospheres Fillite is a glass hard, inert, hollow silicate sphere. Fillite is primarily used to reduce the weight of plastics, rubbers, resins, cement, etc., but also imparts further benefits in many situatio.. |
|||
| Particle Size | 5.0 - 7.0 µm | 5.0 - 7.0 µm | Grain Size; Intercept Method |
| CoorsTek ADOS-90R 91% Alumina Thick Film Substrate This 91-percent alumina (nominal) formulation offers a dark brown body for special applications. Applications: thick films and lasers |
|||
| Particle Size | 5.0 - 10 µm | 5.0 - 10 µm | Mean particle size |
| Carborundum CarboTherm™ CTF5 Boron Nitride Powder Boron Nitride powders have high thermal conductivity, low dielectric loss, and low thermal expansion. They are non-abrading to electronic components, lubricious, non-toxic, and retain their dielect.. |
|||
| Particle Size | 5.0 µm | 5.0 µm | Loosely agglomerated |
| Arkema Group KYNAR® 741 Polyvinylidene Fluoride Powder Characteristics: White, non-hygroscopic powder. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mechanical strength, low permeability, abrasion resistan.. |
|||
| Particle Size | 5.0 µm | 5.0 µm | |
| Poco Graphite Glassmate® HT Graphite This high strength material has an oxidation inhibitor that raises the oxidation threshold. Service temperature can be raised to 600°C; graphites are subject to oxidation above 450°C |
|||
| Particle Size | <= 5.0 µm | <= 5.0 µm | Fineness of Grind |
| Gwent Electronic Materials C2040226D2 Curable Carbon Ink This product is based on a unique curing process that results in the low temperature formation of a thermosetting conductive coating that combines good adhesion with excellent chemical, solvent and .. |
|||