Physical Properties | Metric | English | Comments |
---|---|---|---|
Particle Size | <= 32 µm | <= 32 µm | 90% smaller than |
Nyco M325 WOLLASTOCOAT® Wollastonite Wollastonite is a naturally occurring white mineral with an acicular (needle-shaped) particle structure. This distinctive particle morphology makes wollastonite an ideal performance mineral for a br.. |
|||
Particle Size | 32 µm | 32 µm | Average Diameter |
Potters Industries Conduct-O-Fil® S3000-S2E Silver-Coated Solid Glass Spheres Conduct-O-Fil® Conductive Particles are engineered to meet a broad range of conductive and electro magnetic interference requirements. Applications include EMI shielding, conductive adhesives, Z-a.. |
|||
Particle Size | 32 µm | 32 µm | Average Diameter |
Potters Industries Conduct-O-Fil® S3000-S3E Silver-Coated Solid Glass Spheres Conduct-O-Fil® Conductive Particles are engineered to meet a broad range of conductive and electro magnetic interference requirements. Applications include EMI shielding, conductive adhesives, Z-a.. |
|||
Particle Size | 32 µm | 32 µm | 20% max, wet sieve |
Magyar Aluminum ALO-P90-06 Alumina Alumina for Polishing |
|||
Particle Size | 32 - 44 µm | 32 - 44 µm | d90 |
Indium Corp. Standard ITO Indium Tin Oxide Indium Tin Oxide (ITO, or tin-doped indium oxide) is a mixture of indium(III) oxide and tin(IV) oxide, typically 90% indium oxide, 10% tin oxide by weight. In powder form it is yellow-green in colo.. |
|||
Particle Size | 32 - 42 µm | 32 - 42 µm | 50% |
H.C. Starck Amperit® 140.1 Tungsten (W) HS Number: 81011000 |
|||
Particle Size | 32 - 38 µm | 32 - 38 µm | 50% |
H.C. Starck Amperit® 526.062 Agglomerated, Sintered Tungsten Carbide-Cobalt (WC-Co) 83-17 |
|||
Particle Size | 32 - 38 µm | 32 - 38 µm | 50% |
H.C. Starck Amperit® 526.074 Agglomerated, Sintered Tungsten Carbide-Cobalt (WC-Co) 83-17 |
|||
Particle Size | 32 - 40 µm | 32 - 40 µm | 50% |
H.C. Starck Amperit® 554.074 Tungsten Carbide-Cobalt-Chromium 86-10-4 (WC-Co-Cr) |
|||
Particle Size | 32 µm | 32 µm | Maximum of 12% less than for Ni-SF RC 60 |
H.C. Starck Amperit® 560.062 Tungsten Carbide-Cobalt(83-17)-Nickel-SF RC 60 50-50 (Wc-Co / NiSF RC 60) Composition is of NiSF RC 60 only |
|||
Particle Size | 32 - 38 µm | 32 - 38 µm | 50% for WC-Co 83-17 |
H.C. Starck Amperit® 560.062 Tungsten Carbide-Cobalt(83-17)-Nickel-SF RC 60 50-50 (Wc-Co / NiSF RC 60) Composition is of NiSF RC 60 only |
|||
Particle Size | 32 µm | 32 µm | Maximum of 7% less than, WSC-Ni 92/8 |
H.C. Starck Amperit® 568.005 Tungsten Carbide-Nickel 92-8 - Nickel SF RC 60 65-35 Composition is of NiSF RC 60 only |
|||
Particle Size | 32 - 40 µm | 32 - 40 µm | 50% |
H.C. Starck Amperit® 586.054 Chromium Carbide-Nickel Chromium 80-20 (Cr3C2-NiCr) |
|||
Particle Size | 32 - 48 µm | 32 - 48 µm | |
Lucite International Colacryl ® D1-120 Acrylic Dental Resin Cold-curing denture repair resin with Methyl Methacrylate based copolymers. Features fast polymerisation, easy mixing, good clarity, short hydroflask cure cycles, and excellent pigment acceptance.I.. |
|||
Particle Size | <= 32 µm | <= 32 µm | 74% |
SGL Carbon Group CF 1135 Carbon Filler Good mechanical strength, good sliding properties, high temperature resistance, high thermal shock resistance, low wettability, high corrosion resistance, high thermal conductivity, high purity, and.. |
|||
Particle Size | <= 32 µm | <= 32 µm | 67% |
SGL Carbon Group CF 270 Graphite Filler Good mechanical strength, good sliding properties, high temperature resistance, high thermal shock resistance, low wettability, high corrosion resistance, high thermal conductivity, high purity, and.. |
|||
Particle Size | <= 32 µm | <= 32 µm | 78% |
SGL Carbon Group CF 3100 Graphite Filler Good mechanical strength, good sliding properties, high temperature resistance, high thermal shock resistance, low wettability, high corrosion resistance, high thermal conductivity, high purity, and.. |
|||
Particle Size | <= 32 µm | <= 32 µm | 57% |
SGL Carbon Group CF 480 Graphite Filler Good mechanical strength, good sliding properties, high temperature resistance, high thermal shock resistance, low wettability, high corrosion resistance, high thermal conductivity, high purity, and.. |
|||
Particle Size | <= 32 µm | <= 32 µm | 60% |
SGL Carbon Group CF 5250 Carbon Filler Good mechanical strength, good sliding properties, high temperature resistance, high thermal shock resistance, low wettability, high corrosion resistance, high thermal conductivity, high purity, and.. |
|||
Particle Size | 32 µm | 32 µm | @ 98% |
CIMBAR RiverCal™ 8107 & 8107C Calcium Carbonate (CaCO3) RiverCal™ 8100 Series Calcium Carbonate are high purity, white, functional fillers targeted for use in thermosets, thermoplastics, paint & coatings, sealants, TPO's and TPE's and other applications.. |