Physical Properties | Metric | English | Comments |
---|---|---|---|
Particle Size | <= 22 µm | <= 22 µm | 90% smaller than |
Nyco 400 WOLLASTOCOAT® Wollastonite This grade is recommended for polymer reinforcement.Wollastonite is a naturally occurring white mineral with an acicular (needle-shaped) particle structure. This distinctive particle morphology make.. |
|||
Particle Size | 22 µm | 22 µm | Median Diameter |
Omya PULPROWHITE® 20 - SA Calcium Carbonate A dry ground calcium carbonate with a medium and closely sized particle distribution and excellent shrink resistance properties.Information supplied by Omya North America. |
|||
Particle Size | 22 µm | 22 µm | Maximum of 15% less than |
H.C. Starck Amperit® 175.1 Nickel (Ni) |
|||
Particle Size | 22 µm | 22 µm | Maximum of 15% less than |
H.C. Starck Amperit® 250.1 Water Atomized (NiCr 80-20) |
|||
Particle Size | 22 µm | 22 µm | Maximum of 22% less than |
H.C. Starck Amperit® 250.3 Water Atomized (NiCr 80-20) |
|||
Particle Size | 22 µm | 22 µm | Maximum of 15% less than |
H.C. Starck Amperit® 251.1 Gas Atomized (NiCr 80-20) |
|||
Particle Size | 22 µm | 22 µm | Maximum of 15% less than |
H.C. Starck Amperit® 410.1 Gas Atomized (NiCoCrAlY) |
|||
Particle Size | 22 - 26 µm | 22 - 26 µm | 10% |
H.C. Starck Amperit® 519.088 Agglomerated, Sintered Tungsten Carbide-Cobalt 88-12 (WC-CO) |
|||
Particle Size | 22 - 26 µm | 22 - 26 µm | 10% |
H.C. Starck Amperit® 526.088 Agglomerated, Sintered Tungsten Carbide-Cobalt (WC-Co) 83-17 |
|||
Particle Size | 22 - 26 µm | 22 - 26 µm | 10% |
H.C. Starck Amperit® 527.088 Agglomerated, Sintered Tungsten Carbide-Cobalt (WC-Co) 83-17 |
|||
Particle Size | 22 - 30 µm | 22 - 30 µm | 50% |
H.C. Starck Amperit® 584.072 Chromium Carbide-Nickel-Chromium 75-25 (Cr3C2-NiCr) |
|||
Particle Size | <= 22 µm | <= 22 µm | >85% for MIM |
H.C. Starck CuNi 97/3 Atomized Powder Ni- and FE based alloys for special P/M, HIP and MIM parts, Cu based alloys for brazing. |
|||
Particle Size | <= 22 µm | <= 22 µm | >85% for MIM |
H.C. Starck FeNiCo Atomized Powder Ni- and FE based alloys for special P/M, HIP and MIM parts, Cu based alloys for brazing. |
|||
Particle Size | <= 22 µm | <= 22 µm | >85% for MIM |
H.C. Starck NiAl 97/3 Atomized Powder Ni- and FE based alloys for special P/M, HIP and MIM parts, Cu based alloys for brazing. |
|||
Particle Size | 22 µm | 22 µm | 100% less than |
H.C. Starck Amperit® 704.067 Chromium Oxide (Cr2O3) 99.5% |
|||
Particle Size | 22 µm | 22 µm | Maximum of 10% less than |
H.C. Starck Amperit® 704.092 Chromium Oxide (Cr2O3) 99.5% |
|||
Particle Size | 22 µm | 22 µm | |
Silberline Sparkle Silver® Premier 313AR Sparkle Silver® Premier flakes provide more uniform surfaces than Sparkle Silver® products, and also sharper edges and controlled particle size distribution. "Sparkle Silver® Premier or Sil.. |
|||
Particle Size | 22 µm | 22 µm | |
Silberline Sparkle Silver® Premier 454 Sparkle Silver® Premier flakes provide more uniform surfaces than Sparkle Silver® products, and also sharper edges and controlled particle size distribution. "Sparkle Silver® Premier or Sil.. |
|||
Particle Size | 22 µm | 22 µm | d90 |
TIMCAL TIMREX® MK25 Primary Synthetic Graphite TIMREX Primary Synthetic Graphite is produced in a unique highly controlled graphitization process which assures narrow specifications and unequalled consistent quality due to: monitoring of all pro.. |
|||
Particle Size | 22 µm | 22 µm | d90 |
TIMCAL TIMREX® PG25 Natural P/M Special-Graphite TIMREX Natural Flake Graphite is produced in a wide range of products distinguished by particle size distribution, chemistry and carbon content. Timcal mines the graphite from its own source in Lac-.. |
|||
Particle Size | 22 µm | 22 µm | @ 90% |
CIMBAR MV 610 Talc MV Series talcs are produced from high purity talc ore, which provide good color, acid resistance and excellent barrier properties when used in paint & coating formulations. MV Series talcs are pla.. |
|||
Particle Size | 22 µm | 22 µm | Maximum of 15% less than |
H.C. Starck Amperit® 415.1 CoNiCrAlY (MCrAlY) |
|||
Particle Size | 22 µm | 22 µm | Maximum of 15% less than |
H.C. Starck Amperit® 421.1 NiCoCrAlTaReY (MCrAlY) |
|||
Particle Size | 22 - 26 µm | 22 - 26 µm | 10% |
H.C. Starck Amperit® 588.088 Chromium Carbide-Nickel Chromium 75-25 (Cr3C2-NiCr) 53/20 µm |
|||
Particle Size | 22 - 26 µm | 22 - 26 µm | 10% |
H.C. Starck Amperit® 547.074 Tungsten Carbide-Nickel 88-12 (WC-Ni) |
|||
Particle Size | 22 - 28 µm | 22 - 28 µm | 50% |
H.C. Starck Amperit® 552.072 Tungsten Carbide - Chromium Carbide-Nickel 73-20-7 (WC-CrC-Ni) |
|||
Particle Size | 22 - 30 µm | 22 - 30 µm | 10% |
H.C. Starck Amperit® 584.054 Chromium Carbide-Nickel Chromium 75-25 (Cr3C2-NiCr) |