Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | >= 0.0150 g/cc | >= 0.000542 lb/in³ | Minimum apparent density on a continuous pre-expander after one expansion |
Polimeri Europa Extir® Verdi VR A5000 AE Expandable Polystyrene - Flame Retardant b>Product Description:Extir Verdi VR A5000 AE is a flame-retardant expandable polystyrene in the form of spherical beads of medium-large particle size, containing pentane as blowing agent.Extir does.. |
|||
Density | 0.0150 - 0.0250 g/cc | 0.000542 - 0.000903 lb/in³ | Normal range, one pre-expansion |
SABIC EPS 650FF Expandable Polystyrene Product Description: Fire retardant expanded Polystyrene EPS 650FF is manufactured by the suspension polymerization of styrene monomer. The polymerization is generally carried out in a batch proce.. |
|||
Density | 0.0150 - 0.0200 g/cc | 0.000542 - 0.000723 lb/in³ | Normal range, one pre-expansion |
SABIC EPS 760FF Expandable Polystyrene Product Description: Fire retardant expanded Polystyrene EPS 760FF is manufactured by the suspension polymerization of styrene monomer. The polymerization is generally carried out in a batch proce.. |
|||
Density | 0.0150 - 0.0200 g/cc | 0.000542 - 0.000723 lb/in³ | Normal range, one pre-expansion |
SABIC EPS 763 Expandable Polystyrene Product Description: Standard expanded Polystyrene EPS 763 is manufactured by the suspension polymerization of styrene monomer. The polymerization is generally carried out in a batch process. EPS.. |
|||
Density | 0.0150 - 0.0300 g/cc | 0.000542 - 0.00108 lb/in³ | Pressurized batch pre-foamer; Usual Use |
NOVA Chemicals Gedexcel® 64XA Expandable Polystyrene Styrene homopolymer containing pentane, used as a blowing agent with an additive improving its reaction to fire. Fast molding cycle product for molding blocks f average and low densities.Information.. |
|||
Density | 0.0150 - 0.0250 g/cc | 0.000542 - 0.000903 lb/in³ | Usual Use |
NOVA Chemicals Gedexcel® 65XA Expandable Polystyrene Styrene homopolymer containing pentane, used as a blowing agent with an additive improving its reaction to fire. Fast molding cycle product for molding blocks of average and low densities.Informati.. |
|||
Density | 0.0150 - 0.0200 g/cc | 0.000542 - 0.000723 lb/in³ | Pressurized batch pre-foamer; Usual Use |
NOVA Chemicals Gedexcel® 74XA Expandable Polystyrene Styrene homopolymer containing pentane, sued as a blowing agent with an additive improving its reaction to fire. Fast molding cycle product for molding blocks of average and low densities.Informatio.. |
|||
Density | >= 0.0150 g/cc | >= 0.000542 lb/in³ | Minimum apparent density on a continuous pre-expander after one expansion |
Polimeri Europa Extir® CM Giotto 5 AE Expandable Polystyrene - Continuous Mass/Flame Retardant Product Description:Extir CM is the new expandable products range produced with the new Continuous Mass technology. All the products have a very low dimensional dispersion and a reduced content of .. |
|||
Density | 0.0150 - 0.0500 g/cc | 0.000542 - 0.00181 lb/in³ | |
Polimeri Europa Extir® E 5000 AE Expandable Polystyrene
(discontinued **) Extir E 5000 AE is a flame-retardant expandable polystyrene in the form of spherical beads of medium-large particle size, with a low pentane content as blowing agent. Extir does not contain CFC or H.. |
|||
Density | >= 0.0150 g/cc | >= 0.000542 lb/in³ | Minimum achievable; Single stage pre-expansion in continuous expander at atmospheric pressure |
Ineos Nova T523C Expandable Polystyrene A fast expanding regular molding grade consisting of spherical polystyrene beads containing pentane as expansion agent typically used for medium density foam.Applications: This grade is used mainly .. |
|||
Density | 0.0150 - 0.0300 g/cc | 0.000542 - 0.00108 lb/in³ | Normal molded density assuming cost optimized selection of processing conditions. |
Ineos Nova T523C Expandable Polystyrene A fast expanding regular molding grade consisting of spherical polystyrene beads containing pentane as expansion agent typically used for medium density foam.Applications: This grade is used mainly .. |
|||
Density | >= 0.0150 g/cc | >= 0.000542 lb/in³ | Minimum achievable; Single stage pre-expansion in continuous expander at atmospheric pressure |
Ineos Nova T543B Expandable Polystyrene A fast expanding regular molding grade consisting of spherical polystyrene beads containing pentane as expansion agent typically used for medium density foam.Applications: This grade is used mainly .. |
|||
Density | 0.0150 - 0.0300 g/cc | 0.000542 - 0.00108 lb/in³ | Normal molded density assuming cost optimized selection of processing conditions. |
Ineos Nova T543B Expandable Polystyrene A fast expanding regular molding grade consisting of spherical polystyrene beads containing pentane as expansion agent typically used for medium density foam.Applications: This grade is used mainly .. |
|||
Density | 0.0150 - 0.0160 g/cc | 0.000542 - 0.000578 lb/in³ | |
IRPC Polimaxx Pentfoam 361F Expandable Polystyrene GENERAL: PENTFOAM "361F" IS A REGULAR GRADE (STANDARD GRADE) EXPANDABLE POLYSTYRENE (EPS) CONTAINING PENTANE AS BLOWING AGENT. THIS GRADE IS DEVELOPED TO MEET THE DEMAND FOR FAST MOLDING CYCLES IN V.. |
|||
Density | 0.0150 g/cc | 0.000542 lb/in³ | 150 second cycle time |
Jackon JACKOCELL® S2314 Expanded Polystyrene Construction and Block Molding 100% PolystyrenePre-expansionThis is the low pentane version for high quality block molding.Block MouldingJackocell® S2314 represents the favorite choice for the manufacture of high quality insul.. |
|||
Density | 0.0150 g/cc | 0.000542 lb/in³ | Nominal skin/skin; BS ISO 7214 1998 |
Zotefoams Plastazote® LD15FM Low Density Polyethylene Foam, Flame Retarded Plastazote® is a closed cell, cross-linked polyethylene foam manufactured using nitrogen expansion technology to produce foams with exceptional cell size uniformity, low odor / high purity and outs.. |
|||
Density | 0.0150 g/cc | 0.000542 lb/in³ | Nominal skin/skin; BS ISO 7214 1998 |
Zotefoams Plastazote® MP15FR Metallocene Polyethylene Foam, Flame Retardant Plastazote® is a closed cell, cross-linked polyethylene foam manufactured using nitrogen expansion technology to produce foams with exceptional cell size uniformity, low odor / high purity and outs.. |
|||
Density | <= 0.0150 g/cc | <= 0.000542 lb/in³ | TMA |
Akzo Nobel Expancel® 006 WUF 40 Wet unexpanded microspheres Expancel microspheres are thermoplastic hollow spheres. The microspheres are white spherically formed particles with a thermoplastic shell encapsulating a gas. When the microspheres are heated the.. |
|||
Density | <= 0.0150 g/cc | <= 0.000542 lb/in³ | TMA |
Akzo Nobel Expancel® 007 WUF 40 Wet unexpanded microspheres Expancel microspheres are thermoplastic hollow spheres. The microspheres are white spherically formed particles with a thermoplastic shell encapsulating a gas. When the microspheres are heated the.. |
|||
Density | 0.0150 - 0.0800 g/cc | 0.000542 - 0.00289 lb/in³ | |
BASF Styropor® BFL 322 EPS Description: Modified expandable polystyrene (EPS) containing approximately 3.75 – 3.95 wt% pentane as the blowing agent. Styropor BFL products are compatible with many anti-stat, mineral oil and c.. |
|||
Density | 0.0150 g/cc | 0.000542 lb/in³ | Nominal skin/skin; BS ISO 7214 1998 |
Zotefoams Plastazote® LD15 Low Density Polyethylene Foam Plastazote® is a closed cell, cross-linked polyethylene foam manufactured using nitrogen expansion technology to produce foams with exceptional cell size uniformity, low odor / high purity and outs.. |
|||
Density | 0.0150 - 0.0480 g/cc | 0.000542 - 0.00173 lb/in³ | |
BASF Styropor® BF 322 EPS Description: Modified expandable polystyrene (EPS) containing approximately 6 wt% pentane as the blowing agent. Styropor BF products are compatible with many anti-stat, mineral oil and color additiv.. |
|||
Density | 0.0150 g/cc | 0.000542 lb/in³ | 90 second cycle time |
Jackon JACKOCELL® S314 Expanded Polystyrene Construction and Block Molding Pre-ExpansionThe unique design of polystyrene chains and additive chemistry in Jackocell® S314 gives pre-expanded beads high dimensional stability even at low densities, which typically reduces ave.. |