Polymer Property : Density = 8.75 g/cc Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Physical Properties	Metric	English	Comments
Density	8.75 g/cc	0.316 lb/inÂ³
Lucas-Milhaupt SilvaloyÂ® 30 Brazing Alloy Silvaloy 30 is historically a modification of Silvaloy 35 with further reduction in silver content resulting in a higher melting point and a longer range. Silvaloy 30 is used for brazing steel, stai..
Density	8.75 g/cc	0.316 lb/inÂ³
Haynes HastelloyÂ® S alloy, flat products, solution heat-treated at 538Â°C (1000Â°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093Â°C, good high temperature and thermal fatigue strength. Application..
Density	8.75 g/cc	0.316 lb/inÂ³
Haynes HastelloyÂ® S alloy, flat products, solution heat-treated at 649Â°C (1200Â°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093Â°C, good high temperature and thermal fatigue strength. Application..
Density	8.75 g/cc	0.316 lb/inÂ³
Haynes HastelloyÂ® S alloy, flat products, solution heat-treated at 649Â°C (1200Â°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093Â°C, good high temperature and thermal fatigue strength. Application..
Density	8.75 g/cc	0.316 lb/inÂ³
Haynes HastelloyÂ® S alloy, flat products, solution heat-treated at 760Â°C (1400Â°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093Â°C, good high temperature and thermal fatigue strength. Application..
Density	8.75 g/cc	0.316 lb/inÂ³
Haynes HastelloyÂ® S alloy, gas tungsten arc welded Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093Â°C, good high temperature and thermal fatigue strength. Application..
Density	8.75 g/cc	0.316 lb/inÂ³
Haynes HastelloyÂ® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick, aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093Â°C, good high temperature and thermal fatigue strength. Application..
Density	8.75 g/cc	0.316 lb/inÂ³
Haynes HastelloyÂ® S alloy, gas tungsten arc welded, aged at 538Â°C (1000Â°F) for 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093Â°C, good high temperature and thermal fatigue strength. Application..
Density	8.75 g/cc	0.316 lb/inÂ³
Haynes HastelloyÂ® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427Â°C (800Â°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093Â°C, good high temperature and thermal fatigue strength. Application..
Density	8.75 g/cc	0.316 lb/inÂ³
Haynes HastelloyÂ® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871Â°C (1600Â°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093Â°C, good high temperature and thermal fatigue strength. Application..
Density	8.75 g/cc	0.316 lb/inÂ³
Haynes HastelloyÂ® S alloy, weld metal, aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093Â°C, good high temperature and thermal fatigue strength. Application..
Density	8.75 g/cc	0.316 lb/in³
Universal Wire Works No. 1 Cobalt Alloy Welding Wire Universal No. 1 is a cobalt-chromium-tungsten alloy suited for applications requiring extreme abrasion resistance at elevated temperatures. Excellent for resistance to corrosion and oxidation where ..
Density	8.75 g/cc	0.316 lb/in³	Annealed
Eagle Brass 230 Red Brass, 1/4 Hard CDA 230 is known for having an electrical conductivity of 37% IACS, red color, corrosion resistance, excellent formability and moderate strength. Typical uses include costume jewelry, eyelets, faste..
Density	8.75 g/cc	0.316 lb/in³	Annealed
Eagle Brass 230 Red Brass, 3/4 Hard CDA 230 is known for having an electrical conductivity of 37% IACS, red color, corrosion resistance, excellent formability and moderate strength. Typical uses include costume jewelry, eyelets, faste..
Density	8.75 g/cc	0.316 lb/in³	Annealed
Eagle Brass 230 Red Brass, Annealed CDA 230 is known for having an electrical conductivity of 37% IACS, red color, corrosion resistance, excellent formability and moderate strength. Typical uses include costume jewelry, eyelets, faste..
Density	8.75 g/cc	0.316 lb/in³	Annealed
Eagle Brass 230 Red Brass, Spring CDA 230 is known for having an electrical conductivity of 37% IACS, red color, corrosion resistance, excellent formability and moderate strength. Typical uses include costume jewelry, eyelets, faste..
Density	8.75 g/cc	0.316 lb/in³	Annealed
Eagle Brass 752 Nickel Silver 18%, 1/4 Hard Alloy C752 combines corrosion resistance with strength and a lustrous silver color. Applications include optical frames and parts, springs, surgical instruments, jewelry, resistors and contacts.Info..
Density	8.75 g/cc	0.316 lb/in³	Annealed
Eagle Brass 752 Nickel Silver 18%, Annealed Alloy C752 combines corrosion resistance with strength and a lustrous silver color. Applications include optical frames and parts, springs, surgical instruments, jewelry, resistors and contacts.Info..
Density	8.75 g/cc	0.316 lb/in³	Annealed
Eagle Brass 752 Nickel Silver 18%, Extra Spring Alloy C752 combines corrosion resistance with strength and a lustrous silver color. Applications include optical frames and parts, springs, surgical instruments, jewelry, resistors and contacts.Info..
Density	8.75 g/cc	0.316 lb/in³
CMW® 100 Copper Alloy CMW® 100 material is a heat treatable, high strength, high conductivity copper base alloy. Its properties are a combination of highest strength and hardness with relatively high electrical and ther..
Density	8.75 g/cc	0.316 lb/in³
CMW® 353 Copper Alloy CMW® 353 material is an economical high strength, high conductivity copper base alloy. It is a heat treatable copper base alloy and its excellent properties are obtained largely through heat treatm..
Density	8.75 g/cc	0.316 lb/in³
Cadi C17500 Copper Alloy Information provided by Cadi Company.
Density	8.75 g/cc	0.316 lb/in³
California Fine Wire Permanickel® K-300 Nickel Alloy All values may vary dependent on specific design and usagePermanickel® is a registered trade name of the Inco family of products.Capabilities: WireRibbonInsulatedPlatedInformation provided by Calif..
Density	8.75 g/cc	0.316 lb/in³
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications ..
Density	8.75 g/cc	0.316 lb/in³
Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications ..
Density	8.75 g/cc	0.316 lb/in³
Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications ..