Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 1.245 g/cc | 0.04498 lb/in³ | ASTM D792 |
SABIC Innovative Plastics Lexan® 500 PC 10% GR PC. Optimum combination of high modulus plus excellent impact strength and flame retardance. |
|||
Density | 1.245 g/cc | 0.04498 lb/in³ | ASTM D792 |
SABIC Innovative Plastics Lexan® 500 PC (Asia Pacific) 10% GR PC. Optimum combination of high modulus plus excellent impact strength and flame retardance. |
|||
Density | 1.245 g/cc | 0.04498 lb/in³ | ASTM D792 |
SABIC Innovative Plastics Lexan® 500R PC 10% GR PC. Optimum combination of high modulus plus excellent impact strength and flame retardance. Internal mold release. |
|||
Density | 1.245 g/cc | 0.04498 lb/in³ | ASTM D792 |
SABIC Innovative Plastics Lexan® 500R PC (Asia Pacific) 10% GR PC. Optimum combination of high modulus plus excellent impact strength and flame retardance. Internal mold release. |
|||
Density | 1.245 g/cc | 0.04498 lb/in³ | ASTM D792 |
SABIC Innovative Plastics Lexan® 503 PC 10% GR PC. Optimum combination of high modulus plus excellent impact strength and flame retardance. UV-stabilized. |
|||
Density | 1.245 g/cc | 0.04498 lb/in³ | ASTM D792 |
SABIC Innovative Plastics Lexan® 503 PC (Asia Pacific) 10% GR PC. Optimum combination of high modulus plus excellent impact strength and flame retardance. UV-stabilized. |
|||
Density | 1.245 g/cc | 0.04498 lb/in³ | ASTM D792 |
SABIC Innovative Plastics Lexan® 503R PC 10% GR PC. Optimum combination of high modulus plus excellent impact strength and flame retardance. UV-stabilized. Internal mold release. |
|||
Density | 1.245 g/cc | 0.04498 lb/in³ | ASTM D792 |
SABIC Innovative Plastics Lexan® 503R PC (Asia Pacific) 10% GR PC. Optimum combination of high modulus plus excellent impact strength and flame retardance. UV-stabilized. Internal mold release. |
|||
Density | 1.245 g/cc @Temperature 25.0 °C |
0.04498 lb/in³ @Temperature 77.0 °F |
|
Shandong Dongyue Polymer HFC-125 Pentafluoroethane Refrigerant, CHF2CF3 Usage: Component of mixture used as refrigerant substituting for CFC-502 and HCFC-22; Fire extinguishing agent substituting for Halon-1211 and Halon-1301Packing: Transport by cylinder or tank, the l.. |
|||
Density | 1.245 g/cc | 0.04498 lb/in³ | ISO 1183 |
Stir SpA C 2036 DS AT (PVC) Application: Molding for solesInformation provided by STIR SpA |
|||
Density | 1.245 g/cc | 0.04498 lb/in³ | ISO 1183 |
Stir SpA CT 80 ATC R (PVC) Application: Tread, pure plasticInformation provided by STIR SpA |
|||
Density | 1.245 g/cc | 0.04498 lb/in³ | ASTM D792 |
SABIC Innovative Plastics NORYL GTX GTX820 PPE+PS+PA GR 20%. Higher stiffness of 800000 psi (4000 MPa) flexural modulus. Excellent chemical and high heat resistance. Application: valves. |
|||
Density | 1.245 g/cc | 0.04498 lb/in³ | ASTM D792 |
SABIC Innovative Plastics NORYL GTX GTX820 PPE+PS+PA (Asia Pacific) GR 20%. Higher stiffness of 800000 psi (4000 MPa) flexural modulus. Excellent chemical and high heat resistance. Application: valves. |