Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 0.0180 - 0.0300 g/cc | 0.000650 - 0.00108 lb/in³ | Density range normally used |
Polimeri Europa Extir® A 2000 AE Expandable Polystyrene, Standard Flame Retardant Particle size range is 0.4 - 75 mm. Minimum apparent density on a discontinuous pre-expander is 17 g/l.Processing technology used for Type A 2000 AE is: Molding, Traditional and Vacuum.Specific cha.. |
|||
Density | 0.0180 - 0.0350 g/cc | 0.000650 - 0.00126 lb/in³ | Density range normally used |
Polimeri Europa Extir® B 3000 AE Expandable Polystyrene, Fast Molding Flame Retardant Particle size range is 0.7 - 1 mm. Minimum apparent density on a discontinuous pre-expander is 17 g/l.Processing technology used for Type B 3000 AE is: Molding, Vacuum.Specific characteristics: DIN.. |
|||
Density | >= 0.0180 g/cc | >= 0.000650 lb/in³ | Minimum apparent density on a continuous pre-expander after one expansion |
Polimeri Europa Extir® CM Galileo Europa 5 AE Expandable Polystyrene - Continuous Mass Product Description:Extir CM is the new expandable products range produced with the new Continuous Mass technology. All the products have a very low dimensional dispersion and a reduced content of .. |
|||
Density | >= 0.0180 g/cc | >= 0.000650 lb/in³ | Minimum apparent density on a continuous pre-expander after one expansion |
Polimeri Europa Extir® CM Galileo Europa 5 Expandable Polystyrene - Continuous Mass Product Description:Extir CM is the new expandable products range produced with the new Continuous Mass technology. All the products have a very low dimensional dispersion and a reduced content of .. |
|||
Density | 0.0180 - 0.0400 g/cc | 0.000650 - 0.00145 lb/in³ | Usual Use |
NOVA Chemicals Gedexcel® 45B Expandable Polystyrene Styrene homopolymer containing pentane, used as a blowing agent. Fast molding cycle product allowing to obtain optimum mechanical properties for form molding of very thin parts (5 mm to 20 mm).Infor.. |
|||
Density | >= 0.0180 g/cc | >= 0.000650 lb/in³ | Minimum apparent density on a continuous pre-expander after one expansion |
Polimeri Europa Extir® CM Galileo Io 5 AE Expandable Polystyrene - Continuous Mass Product Description:Extir CM is the new expandable products range produced with the new Continuous Mass technology. All the products have a very low dimensional dispersion and a reduced content of .. |
|||
Density | >= 0.0180 g/cc | >= 0.000650 lb/in³ | Minimum apparent density on a continuous pre-expander after one expansion |
Polimeri Europa Extir® CM Galileo Io 5 Expandable Polystyrene - Continuous Mass Product Description:Extir CM is the new expandable products range produced with the new Continuous Mass technology. All the products have a very low dimensional dispersion and a reduced content of .. |
|||
Density | >= 0.0180 g/cc | >= 0.000650 lb/in³ | Minimum apparent density on a continuous pre-expander after one expansion |
Polimeri Europa Extir® CM Giotto 5 Expandable Polystyrene - Continuous Mass Product Description:Extir CM is the new expandable products range produced with the new Continuous Mass technology. All the products have a very low dimensional dispersion and a reduced content of .. |
|||
Density | >= 0.0180 g/cc | >= 0.000650 lb/in³ | Minimum apparent density on a continuous pre-expander after one expansion |
Polimeri Europa Extir® D 3000 AE Expandable Polystyrene - Flame Retardant Product Description:Extir D 3000 AE is a flame-retardant expandable polystyrene in the form of spherical beads of medium particle size, containing pentane as blowing agent.Extir does not contain CFC.. |
|||
Density | 0.0180 - 0.0350 g/cc | 0.000650 - 0.00126 lb/in³ | |
Polimeri Europa Extir Leonardo B 3000 AE Expandable Polystyrene
(discontinued **) Extir B 3000 AE is a flame retardant expandable polystyrene in the form of spherical beads of medium particle size, containing pentane as blowing agent. Extir does not contain CFC or HCFC. This grad.. |
|||
Density | 0.0180 - 0.0350 g/cc | 0.000650 - 0.00126 lb/in³ | Density range normally used |
Polimeri Europa Extir® B 3000 Expandable Polystyrene, Fast Molding
(discontinued **) Particle size range is 0.7 - 1 mm. Minimum apparent density on a discontinuous pre-expander is 17 g/l.Processing technology used for Type B 3000 is: Molding, Vacuum.Specific characteristics: Good m.. |
|||
Density | >= 0.0180 g/cc | >= 0.000650 lb/in³ | Minimum achievable; Single stage pre-expansion in continuous expander at atmospheric pressure |
Ineos Nova Styrocell® M544C Expandable Polystyrene A high strength, fast cycling regular molding grade consisting of spherical polystyrene beads containing pentane as expansion agent, typically used for medium density foam.Applications: Styrocell is.. |
|||
Density | 0.0180 - 0.0300 g/cc | 0.000650 - 0.00108 lb/in³ | Final Product Density |
Iran Petrochemical (PCC) TPC - 323 FC Expandable Polystyrene TPC - 323 FCApplications: faster cycling shape molding with wall thickness >10mm, medium to high density blocksInformation provided by Iran Petrochemical Commercial Co. |
|||
Density | 0.0180 - 0.0300 g/cc | 0.000650 - 0.00108 lb/in³ | molding density range |
IRPC Polimaxx Pentfoam 355E Expandable Polystyrene GENERAL: PENTFOAM "355E" IS A SELF EXTINGUISHING (SE) GRADE EXPANDABLE POLYSTYRENE (EPS) CONTAINING PENTANE AS BLOWING AGENT. THIS GRADE IS DEVELOPED TO MEET THE DEMAND FOR FAST EXPANSION RATE AND S.. |
|||
Density | 0.0180 - 0.0300 g/cc | 0.000650 - 0.00108 lb/in³ | molding density range |
IRPC Polimaxx Pentfoam 361F Expandable Polystyrene GENERAL: PENTFOAM "361F" IS A REGULAR GRADE (STANDARD GRADE) EXPANDABLE POLYSTYRENE (EPS) CONTAINING PENTANE AS BLOWING AGENT. THIS GRADE IS DEVELOPED TO MEET THE DEMAND FOR FAST MOLDING CYCLES IN V.. |
|||
Density | 0.0180 g/cc | 0.000650 lb/in³ | 2.4 minute residence time pre-expander |
Jackon JACKOCELL® R411 Expanded Polystyrene Packaging and Shape Molding 100% Polystyrene.Pre-expansionThe unique design of polystyrene chains and additive chemistry in the Jackocell® R411 gives pre-expanded beads of high dimensional stability. The R411 represents the.. |
|||
Density | 0.0180 g/cc | 0.000650 lb/in³ | 1 minute residence time |
Jackon JACKOCELL® S3312 Expanded Polystyrene Packaging and Shape Molding 100% Polystyrene.Pre-expansionA substantial reduced pentane emission has been made possible with Jackocell® S3312 - which will lead the industry into the future. High stability of pre-expanded be.. |
|||
Density | 0.0180 g/cc | 0.000650 lb/in³ | Nominal skin/skin; BS ISO 7214 1998 |
Zotefoams Plastazote® LD18 Low Density Polyethylene Foam Plastazote® is a closed cell, cross-linked polyethylene foam manufactured using nitrogen expansion technology to produce foams with exceptional cell size uniformity, low odor / high purity and outs.. |
|||
Density | 0.0180 - 0.0240 g/cc | 0.000650 - 0.000867 lb/in³ | sheet density |
Zotefoams Plastazote® LD18 Low Density Polyethylene Foam Plastazote® is a closed cell, cross-linked polyethylene foam manufactured using nitrogen expansion technology to produce foams with exceptional cell size uniformity, low odor / high purity and outs.. |
|||
Density | 0.0180 - 0.0240 g/cc | 0.000650 - 0.000867 lb/in³ | sheet density |
Zotefoams Plastazote® LD18SC Low Density Polyethylene Foam, Small Cell Plastazote® is a closed cell, cross-linked polyethylene foam manufactured using nitrogen expansion technology to produce foams with exceptional cell size uniformity, low odor / high purity and outs.. |
|||
Density | 0.0180 - 0.0480 g/cc | 0.000650 - 0.00173 lb/in³ | |
BASF Styropor® BF 422 EPS Description: Modified expandable polystyrene (EPS) containing approximately 6 wt% pentane as the blowing agent. Styropor BF products are compatible with many anti-stat, mineral oil and color additiv.. |
|||
Density | 0.0180 - 0.800 g/cc | 0.000650 - 0.0289 lb/in³ | |
BASF Styropor® BFL 327 EPS Description: Modified expandable polystyrene (EPS) containing approximately 3.75 – 3.95 wt% pentane as the blowing agent. Styropor BFL products are compatible with many anti-stat, mineral oil and c.. |
|||
Density | 0.0180 - 0.0650 g/cc | 0.000650 - 0.00235 lb/in³ | |
BASF Styropor® BFL 422 EPS Description: Modified expandable polystyrene (EPS) containing approximately 3.75 – 3.95 wt% pentane as the blowing agent. Styropor BFL products are compatible with many anti-stat, mineral oil and c.. |
|||
Density | 0.0180 - 0.0300 g/cc | 0.000650 - 0.00108 lb/in³ | Final Product Density |
Iran Petrochemical (PCC) TPC - 326 WP Expandable Polystyrene TPC - 326 WPApplications: low water absorption, longer cycling shape molding with wall thickness >10 mmInformation provided by Iran Petrochemical Commercial Co. |
|||
Density | 0.0180 - 0.0200 g/cc | 0.000650 - 0.000723 lb/in³ | |
IRPC Polimaxx Pentfoam 526W Expandable Polystyrene GENERAL: PENTFOAM "526W" IS A REGULAR GRADE (STANDARD GRADE) EXPANDABLE POLYSTYRENE (EPS) CONTAINING PENTANE AS BLOWING AGENT.APPLICATIONS: PENTFOAM "526W" IS PARTICULARLY WELL SUITED FOR THE MANUFA.. |
|||
Density | 0.0180 g/cc | 0.000650 lb/in³ | 75 second cycle time |
Jackon JACKOCELL® S314 Expanded Polystyrene Construction and Block Molding Pre-ExpansionThe unique design of polystyrene chains and additive chemistry in Jackocell® S314 gives pre-expanded beads high dimensional stability even at low densities, which typically reduces ave.. |
|||
Density | 0.0180 g/cc | 0.000650 lb/in³ | 75 rpm |
Jackon JACKOCELL® S314 Expanded Polystyrene Construction and Block Molding Pre-ExpansionThe unique design of polystyrene chains and additive chemistry in Jackocell® S314 gives pre-expanded beads high dimensional stability even at low densities, which typically reduces ave.. |
|||
Density | 0.0180 - 0.0300 g/cc | 0.000650 - 0.00108 lb/in³ | |
Polimeri Europa Extir Leonardo A 2000 AE Expandable Polystyrene
(discontinued **) Extir A 2000 AE is a flame retardant expandable polystyrene in the form of spherical beads of fine particle size, containing pentane as blowing agent. Extir does not contain CFC or HCFC. Extir A 200.. |
|||
Density | 0.0180 - 0.0350 g/cc | 0.000650 - 0.00126 lb/in³ | Normal range, one pre-expansion |
SABIC EPS 450FF Expandable Polystyrene Product Description: Fire retardant expanded Polystyrene EPS 450FF is manufactured by the suspension polymerization of styrene monomer. The polymerization is generally carried out in a batch proce.. |
|||
Density | 0.0180 - 0.0220 g/cc | 0.000650 - 0.000795 lb/in³ | |
IRPC Polimaxx Pentfoam 328H Expandable Polystyrene General: Pentfoam 328H is a high density grade expandable polystyrene containing pentane as blowing agent, this grade is developed to meet the demand for fast molding cycles in vacuum machineApplica.. |