Zotefoams ZOTEK® N B50 High Performance Nylon Foam

Category Polymer , Thermoplastic , Nylon , Nylon 6
Manufacturer Zotefoams
Trade Name ZOTEK®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Zotefoams ZOTEK® N B50 High Performance Nylon Foam.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Zotek® N B50 is a closed cell, cross-linked polyamide-6 foam manufactured using nitrogen expansion technology to produce foams with exceptional cell size uniformity, low odor / high purity and outstanding physical attributes.Data from material conditioned for 6 days at 23°C, 50% RHInformation provided by Zotefoams
Physical Properties Metric English Comments
Density 0.0520 g/cc
0.00188 lb/in³
ISO 7214
Moisture Absorption at Equilibrium 2.4 %
2.4 %
ISO 760
Cell Length 0.250 mm
0.00984 in
Mechanical Properties Metric English Comments
Hardness, Shore OO 79
79
ISO 868
Tensile Strength 1.30 MPa
189 psi
ISO 1798
Elongation at Break 70 %
70 %
Flexural Modulus 0.000200 GPa

@Temperature 200 °C
 0.0290 ksi

@Temperature 392 °F
 dry
0.000200 GPa

@Temperature 200 °C
 0.0290 ksi

@Temperature 392 °F
 conditioned
0.00100 GPa

@Temperature 150 °C
 0.145 ksi

@Temperature 302 °F
 dry
0.00100 GPa

@Temperature 150 °C
 0.145 ksi

@Temperature 302 °F
 conditioned
0.00150 GPa

@Temperature 100 °C
 0.218 ksi

@Temperature 212 °F
 conditioned
0.00200 GPa

@Temperature 100 °C
 0.290 ksi

@Temperature 212 °F
 dry
0.00200 GPa

@Temperature 0.000 °C
 0.290 ksi

@Temperature 32.0 °F
 conditioned
0.00200 GPa

@Temperature 50.0 °C
 0.290 ksi

@Temperature 122 °F
 conditioned
0.00700 GPa

@Temperature 50.0 °C
 1.02 ksi

@Temperature 122 °F
 dry
0.0100 GPa

@Temperature 0.000 °C
 1.45 ksi

@Temperature 32.0 °F
 dry
0.0110 GPa

@Temperature -40.0 °C
 1.60 ksi

@Temperature -40.0 °F
 conditioned
0.0120 GPa

@Temperature -40.0 °C
 1.74 ksi

@Temperature -40.0 °F
 dry
Compressive Yield Strength 0.170 MPa

@Strain 10.0 %
 24.7 psi

@Strain 10.0 %
 ISO 7214
0.190 MPa

@Strain 25.0 %
 27.6 psi

@Strain 25.0 %
 ISO 7214
0.225 MPa

@Strain 40.0 %
 32.6 psi

@Strain 40.0 %
 ISO 7214
0.280 MPa

@Strain 50.0 %
 40.6 psi

@Strain 50.0 %
 ISO 7214
Tear Strength 3.00 kN/m
17.1 pli
ISO 8067
Compression Set 12 %

@Time 79200 sec,
Strain 25.0 %
 12 %

@Time 22.0 hour,
Strain 25.0 %
 24 hr recovery; ISO 7214
14 %

@Time 79200 sec,
Strain 25.0 %
 14 %

@Time 22.0 hour,
Strain 25.0 %
 0.5 hr recovery; ISO 7214
24 %

@Time 79200 sec,
Strain 50.0 %
 24 %

@Time 22.0 hour,
Strain 50.0 %
 24 hr recovery; ISO 7214
29 %

@Time 79200 sec,
Strain 50.0 %
 29 %

@Time 22.0 hour,
Strain 50.0 %
 0.5 hr recovery; ISO 7214
Thermal Properties Metric English Comments
Thermal Conductivity 0.0360 W/m-K
0.250 BTU-in/hr-ft²-°F
mean temp of 0°C; ISO 8301
0.0381 W/m-K
0.264 BTU-in/hr-ft²-°F
mean temp of 25°C; ISO 8301
0.0405 W/m-K
0.281 BTU-in/hr-ft²-°F
mean temp of 50°C; ISO 8301
0.0420 W/m-K
0.291 BTU-in/hr-ft²-°F
mean temp of 80°C; ISO 8301
0.0463 W/m-K
0.321 BTU-in/hr-ft²-°F
mean temp of 130°C; ISO 8301
0.0512 W/m-K
0.355 BTU-in/hr-ft²-°F
mean temp of 170°C; ISO 8301
Maximum Service Temperature, Air 205 °C
401 °F
Shrinkage <= 2.0 %

@Temperature 130 °C,
Time 3.60e+6 sec
 <= 2.0 %

@Temperature 266 °F,
Time 1000 hour
<= 2.0 %

@Temperature 160 °C,
Time 36000 sec
 <= 2.0 %

@Temperature 320 °F,
Time 10.0 hour
<= 2.0 %

@Temperature 190 °C,
Time 36000 sec
 <= 2.0 %

@Temperature 374 °F,
Time 10.0 hour
<= 3.0 %

@Temperature 160 °C,
Time 360000 sec
 <= 3.0 %

@Temperature 320 °F,
Time 100 hour
<= 4.0 %

@Temperature 160 °C,
Time 3.60e+6 sec
 <= 4.0 %

@Temperature 320 °F,
Time 1000 hour
<= 5.0 %

@Temperature 190 °C,
Time 360000 sec
 <= 5.0 %

@Temperature 374 °F,
Time 100 hour
Descriptive Properties Value Comments
Flammability Automotive: FMVSS.302
Pass at 4 mm and thicker
Users viewing this material also viewed the following: