Zotefoams Plastazote® MP24 Metallocene Polyethylene Foam

Category	Polymer , Thermoplastic , Polyethylene (PE) , LDPE
Manufacturer	Zotefoams
Trade Name	Plastazote®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Zotefoams Plastazote® MP24 Metallocene Polyethylene Foam.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Plastazote® is a closed cell, cross-linked polyethylene foam manufactured using nitrogen expansion technology to produce foams with exceptional cell size uniformity, low odor / high purity and outstanding physical attributes.Compliant with EC food contact regulations.Information provided by Zotefoams

Physical Properties	Metric	English	Comments
Density	0.0170 - 0.0290 g/cc	0.000614 - 0.00105 lb/in³	sheet density
	0.0240 g/cc	0.000867 lb/in³	Nominal skin/skin; BS ISO 7214 1998
Cell Length	0.100 - 0.300 mm	0.00394 - 0.0118 in
	0.200 mm	0.00787 in	Typical Diameter

Mechanical Properties	Metric	English	Comments
Hardness, Shore OO	36	36	10 mm cell/cell thickness; ISO 868 1985
Tensile Strength	0.590 MPa	85.6 psi	ISO 7214 1998
Elongation at Break	140 %	140 %
Compressive Yield Strength	0.0310 MPa @Strain 10.0 %	4.50 psi @Strain 10.0 %	BS ISO 7214 1998
	0.0500 MPa @Strain 25.0 %	7.25 psi @Strain 25.0 %	BS ISO 7214 1998
	0.0800 MPa @Strain 40.0 %	11.6 psi @Strain 40.0 %	BS ISO 7214 1998
	0.110 MPa @Strain 50.0 %	16.0 psi @Strain 50.0 %	BS ISO 7214 1998
Tear Strength	0.700 kN/m	3.99 pli	BS EN ISO 8067 1995
Compression Set	4.5 % @Time 79200 sec, Strain 25.0 %	4.5 % @Time 22.0 hour, Strain 25.0 %	24 hr recovery; BS ISO 7214 1998
	12 % @Time 79200 sec, Strain 25.0 %	12 % @Time 22.0 hour, Strain 25.0 %	0.5 hr recovery; BS ISO 7214 1998
	19.5 % @Time 79200 sec, Strain 50.0 %	19.5 % @Time 22.0 hour, Strain 50.0 %	24 hr recovery; BS ISO 7214 1998
	28 % @Time 79200 sec, Strain 50.0 %	28 % @Time 22.0 hour, Strain 50.0 %	0.5 hr recovery; BS ISO 7214 1998

Thermal Properties	Metric	English	Comments
Thermal Conductivity	0.0390 W/m-K	0.271 BTU-in/hr-ft²-°F	mean temp of 10°C; ISO 8302 1991
Maximum Service Temperature, Air	95.0 °C	203 °F
Minimum Service Temperature, Air	-70.0 °C	-94.0 °F
Flammability Test	1.9 @Thickness 13.0 mm	1.9 @Thickness 0.512 in	Horizontal Burn Rate, mm/sec; ISO 7214 1998
	2.5 @Thickness 5.00 mm	2.5 @Thickness 0.197 in	Horizontal Burn Rate, mm/sec; ISO 7214 1998

Descriptive Properties	Value	Comments
Flammability	Automotive: FMVSS.302 burn rate	Pass: 8mm and thicker