Zotefoams Plastazote® LD60 Low Density Polyethylene Foam

Category Polymer , Thermoplastic , Polyethylene (PE) , LDPE
Manufacturer Zotefoams
Trade Name Plastazote®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Zotefoams Plastazote® LD60 Low Density Polyethylene Foam.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Plastazote® is a closed cell, cross-linked polyethylene foam manufactured using nitrogen expansion technology to produce foams with exceptional cell size uniformity, low odor / high purity and outstanding physical attributes.Compliant with EC food contact and US FDA regulations.Information provided by Zotefoams
Physical Properties Metric English Comments
Density 0.0510 - 0.0660 g/cc
0.00184 - 0.00238 lb/in³
sheet density
0.0600 g/cc
0.00217 lb/in³
Nominal skin/skin; BS ISO 7214 1998
Cell Length 0.600 mm
0.0236 in
Typical Diameter
0.350 - 0.900 mm
0.0138 - 0.0354 in
Mechanical Properties Metric English Comments
Hardness, Shore OO 70
70
10 mm cell/cell thickness; ISO 868 1985
Tensile Strength 0.650 MPa
94.3 psi
ISO 7214 1998
Elongation at Break 165 %
165 %
Flexural Modulus 0.00170 GPa
0.247 ksi
BS4370, part 4, method 14
Compressive Yield Strength 0.110 MPa

@Strain 10.0 %
16.0 psi

@Strain 10.0 %
BS ISO 7214 1998
0.125 MPa

@Strain 25.0 %
18.1 psi

@Strain 25.0 %
BS ISO 7214 1998
0.164 MPa

@Strain 40.0 %
23.8 psi

@Strain 40.0 %
BS ISO 7214 1998
0.208 MPa

@Strain 50.0 %
30.2 psi

@Strain 50.0 %
BS ISO 7214 1998
Tear Strength 1.72 kN/m
9.81 pli
BS EN ISO 8067 1995
Compression Set 2.0 %

@Time 79200 sec,
Strain 25.0 %
2.0 %

@Time 22.0 hour,
Strain 25.0 %
24 hr recovery; BS ISO 7214 1998
5.5 %

@Time 79200 sec,
Strain 25.0 %
5.5 %

@Time 22.0 hour,
Strain 25.0 %
0.5 hr recovery; BS ISO 7214 1998
6.5 %

@Time 79200 sec,
Strain 50.0 %
6.5 %

@Time 22.0 hour,
Strain 50.0 %
24 hr recovery; BS ISO 7214 1998
14.5 %

@Time 79200 sec,
Strain 50.0 %
14.5 %

@Time 22.0 hour,
Strain 50.0 %
0.5 hr recovery; BS ISO 7214 1998
Thermal Properties Metric English Comments
Thermal Conductivity 0.0518 W/m-K
0.359 BTU-in/hr-ft²-°F
mean temp of 10°C; ISO 8302 1991
Maximum Service Temperature, Air 105 °C
221 °F
Minimum Service Temperature, Air -70.0 °C
-94.0 °F
Flammability Test 0.50

@Thickness 13.0 mm
0.50

@Thickness 0.512 in
Horizontal Burn Rate, mm/sec; ISO 7214 1998
1.0

@Thickness 5.00 mm
1.0

@Thickness 0.197 in
Horizontal Burn Rate, mm/sec; ISO 7214 1998