Zotefoams Plastazote® LD50CN Conductive Low Density Polyethylene Foam

Category Polymer , Thermoplastic , Polyethylene (PE) , LDPE
Manufacturer Zotefoams
Trade Name Plastazote®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Zotefoams Plastazote® LD50CN Conductive Low Density Polyethylene Foam.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Plastazote® is a closed cell, cross-linked polyethylene foam manufactured using nitrogen expansion technology to produce foams with exceptional cell size uniformity, low odor / high purity and outstanding physical attributes.Compliant with EC food contact and US FDA regulations.Information provided by Zotefoams
Physical Properties Metric English Comments
Density 0.0500 g/cc
0.00181 lb/in³
Nominal skin/skin; BS ISO 7214 1998
0.0430 - 0.0580 g/cc
0.00155 - 0.00210 lb/in³
sheet density
Cell Length 0.600 - 1.10 mm
0.0236 - 0.0433 in
0.850 mm
0.0335 in
Typical Diameter
Mechanical Properties Metric English Comments
Hardness, Shore OO 73
73
10 mm cell/cell thickness; ISO 868 1985
Tensile Strength 0.515 MPa
74.7 psi
ISO 7214 1998
Elongation at Break 65 %
65 %
Compressive Yield Strength 0.120 MPa

@Strain 10.0 %
17.4 psi

@Strain 10.0 %
BS ISO 7214 1998
0.139 MPa

@Strain 25.0 %
20.2 psi

@Strain 25.0 %
BS ISO 7214 1998
0.172 MPa

@Strain 40.0 %
24.9 psi

@Strain 40.0 %
BS ISO 7214 1998
0.214 MPa

@Strain 50.0 %
31.0 psi

@Strain 50.0 %
BS ISO 7214 1998
Tear Strength 0.800 kN/m
4.56 pli
BS EN ISO 8067 1995
Compression Set 3.5 %

@Time 79200 sec,
Strain 25.0 %
3.5 %

@Time 22.0 hour,
Strain 25.0 %
24 hr recovery; BS ISO 7214 1998
7.5 %

@Time 79200 sec,
Strain 25.0 %
7.5 %

@Time 22.0 hour,
Strain 25.0 %
0.5 hr recovery; BS ISO 7214 1998
10 %

@Time 79200 sec,
Strain 50.0 %
10 %

@Time 22.0 hour,
Strain 50.0 %
24 hr recovery; BS ISO 7214 1998
16 %

@Time 79200 sec,
Strain 50.0 %
16 %

@Time 22.0 hour,
Strain 50.0 %
0.5 hr recovery; BS ISO 7214 1998
Thermal Properties Metric English Comments
Thermal Conductivity 0.0420 W/m-K
0.291 BTU-in/hr-ft²-°F
mean temp of 10°C; ISO 8302 1991
Maximum Service Temperature, Air 105 °C
221 °F
Minimum Service Temperature, Air -70.0 °C
-94.0 °F
Flammability Test 0.70

@Thickness 13.0 mm
0.70

@Thickness 0.512 in
Horizontal Burn Rate, mm/sec; ISO 7214 1998
1.0

@Thickness 5.00 mm
1.0

@Thickness 0.197 in
Horizontal Burn Rate, mm/sec; ISO 7214 1998
Electrical Properties Metric English Comments
Volume Resistivity 1000 ohm-cm
1000 ohm-cm
ASTM D991-89