Zotefoams Plastazote® LD45FR Low Density Polyethylene Foam, Flame Retardant
| Category | Polymer , Thermoplastic , Polyethylene (PE) , LDPE |
| Manufacturer | Zotefoams |
| Trade Name | Plastazote® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Zotefoams Plastazote® LD45FR Low Density Polyethylene Foam, Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Plastazote® is a closed cell, cross-linked polyethylene foam manufactured using nitrogen expansion technology to produce foams with exceptional cell size uniformity, low odor / high purity and outstanding physical attributes.Compliant with EC food contact and US FDA regulations.Information provided by Zotefoams
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.0390 - 0.0490 g/cc | 0.00141 - 0.00177 lb/in³ | sheet density |
| 0.0450 g/cc | 0.00163 lb/in³ | Nominal skin/skin; BS ISO 7214 1998 | |
| Cell Length | 0.400 mm | 0.0157 in | Typical Diameter |
| 0.250 - 0.600 mm | 0.00984 - 0.0236 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore OO | 60 | 60 | 10 mm cell/cell thickness; ISO 868 1985 |
| Tensile Strength | 0.435 MPa | 63.1 psi | ISO 7214 1998 |
| Elongation at Break | 180 % | 180 % | |
| Compressive Yield Strength | 0.0690 MPa @Strain 10.0 % |
10.0 psi @Strain 10.0 % |
BS ISO 7214 1998 |
| 0.0860 MPa @Strain 25.0 % |
12.5 psi @Strain 25.0 % |
BS ISO 7214 1998 | |
| 0.121 MPa @Strain 40.0 % |
17.5 psi @Strain 40.0 % |
BS ISO 7214 1998 | |
| 0.159 MPa @Strain 50.0 % |
23.1 psi @Strain 50.0 % |
BS ISO 7214 1998 | |
| Tear Strength | 1.20 kN/m | 6.85 pli | BS EN ISO 8067 1995 |
| Compression Set | 2.5 % @Time 79200 sec, Strain 25.0 % |
2.5 % @Time 22.0 hour, Strain 25.0 % |
24 hr recovery; BS ISO 7214 1998 |
| 8.5 % @Time 79200 sec, Strain 25.0 % |
8.5 % @Time 22.0 hour, Strain 25.0 % |
0.5 hr recovery; BS ISO 7214 1998 | |
| 11 % @Time 79200 sec, Strain 50.0 % |
11 % @Time 22.0 hour, Strain 50.0 % |
24 hr recovery; BS ISO 7214 1998 | |
| 20 % @Time 79200 sec, Strain 50.0 % |
20 % @Time 22.0 hour, Strain 50.0 % |
0.5 hr recovery; BS ISO 7214 1998 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 0.0430 W/m-K | 0.298 BTU-in/hr-ft²-°F | mean temp of 10°C; ISO 8302 1991 |
| Maximum Service Temperature, Air | 105 °C | 221 °F | |
| Minimum Service Temperature, Air | -70.0 °C | -94.0 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Flammability | Automotive: FMVSS.302 burn rate | Pass: 2 mm and thicker |
| Aviation: CAA8/2-2.2b | Complies | |
| Aviation: FAR-25.853 F 1a. 1ii | Complies | |
| Aviation: JAR-25.853 F 1a. 1ii | Complies | |
| Construction: DIN4102 pt14-B1 | Pass: 6 to 20 mm thick | |
| Construction: UL94 HF1+HF2 | Pass: 3 to 13 mm thick | |
| Horizontal Burn Rate: ISO 7214 1998 | Extinguishes and melts from flame |