Zotefoams Plastazote® LD33 Low Density Polyethylene Foam

Category	Polymer , Thermoplastic , Polyethylene (PE) , LDPE
Manufacturer	Zotefoams
Trade Name	Plastazote®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Zotefoams Plastazote® LD33 Low Density Polyethylene Foam.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Plastazote® is a closed cell, cross-linked polyethylene foam manufactured using nitrogen expansion technology to produce foams with exceptional cell size uniformity, low odor / high purity and outstanding physical attributes.Compliant with EC food contact and US FDA regulations.Information provided by Zotefoams

Physical Properties	Metric	English	Comments
Density	0.0270 - 0.0370 g/cc	0.000975 - 0.00134 lb/in³	sheet density
	0.0330 g/cc	0.00119 lb/in³	Nominal skin/skin; BS ISO 7214 1998
Cell Length	0.370 mm	0.0146 in	Typical Diameter
	0.250 - 0.550 mm	0.00984 - 0.0217 in

Mechanical Properties	Metric	English	Comments
Hardness, Shore OO	58	58	10 mm cell/cell thickness; ISO 868 1985
Tensile Strength	0.440 MPa	63.8 psi	ISO 7214 1998
Elongation at Break	155 %	155 %
Flexural Modulus	0.000700 GPa	0.102 ksi	BS4370, part 4, method 14
Compressive Yield Strength	0.0510 MPa @Strain 10.0 %	7.40 psi @Strain 10.0 %	BS ISO 7214 1998
	0.0690 MPa @Strain 25.0 %	10.0 psi @Strain 25.0 %	BS ISO 7214 1998
	0.102 MPa @Strain 40.0 %	14.8 psi @Strain 40.0 %	BS ISO 7214 1998
	0.137 MPa @Strain 50.0 %	19.9 psi @Strain 50.0 %	BS ISO 7214 1998
Tear Strength	0.785 kN/m	4.48 pli	BS EN ISO 8067 1995
Compression Set	3.0 % @Time 79200 sec, Strain 25.0 %	3.0 % @Time 22.0 hour, Strain 25.0 %	24 hr recovery; BS ISO 7214 1998
	10 % @Time 79200 sec, Strain 25.0 %	10 % @Time 22.0 hour, Strain 25.0 %	0.5 hr recovery; BS ISO 7214 1998
	13.5 % @Time 79200 sec, Strain 50.0 %	13.5 % @Time 22.0 hour, Strain 50.0 %	24 hr recovery; BS ISO 7214 1998
	22.5 % @Time 79200 sec, Strain 50.0 %	22.5 % @Time 22.0 hour, Strain 50.0 %	0.5 hr recovery; BS ISO 7214 1998

Thermal Properties	Metric	English	Comments
Thermal Conductivity	0.0405 W/m-K	0.281 BTU-in/hr-ft²-°F	mean temp of 10°C; ISO 8302 1991
Maximum Service Temperature, Air	100 °C	212 °F
Minimum Service Temperature, Air	-70.0 °C	-94.0 °F
Flammability Test	1.0 @Thickness 13.0 mm	1.0 @Thickness 0.512 in	Horizontal Burn Rate, mm/sec; ISO 7214 1998
	1.6 @Thickness 5.00 mm	1.6 @Thickness 0.197 in	Horizontal Burn Rate, mm/sec; ISO 7214 1998