Zotefoams Plastazote® LD24LC Low Density Polyethylene Foam, Large Cell
| Category | Polymer , Thermoplastic , Polyethylene (PE) , LDPE |
| Manufacturer | Zotefoams |
| Trade Name | Plastazote® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Zotefoams Plastazote® LD24LC Low Density Polyethylene Foam, Large Cell.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Plastazote® is a closed cell, cross-linked polyethylene foam manufactured using nitrogen expansion technology to produce foams with exceptional cell size uniformity, low odor / high purity and outstanding physical attributes.Compliant with EC food contact and US FDA regulations.Information provided by Zotefoams
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.0190 - 0.0250 g/cc | 0.000686 - 0.000903 lb/in³ | sheet density |
| 0.0240 g/cc | 0.000867 lb/in³ | Nominal skin/skin; BS ISO 7214 1998 | |
| Cell Length | 0.900 - 1.60 mm | 0.0354 - 0.0630 in | |
| 1.25 mm | 0.0492 in | Typical Diameter |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore OO | 48 | 48 | 10 mm cell/cell thickness; ISO 868 1985 |
| Tensile Strength | 0.280 MPa | 40.6 psi | ISO 7214 1998 |
| Elongation at Break | 110 % | 110 % | |
| Compressive Yield Strength | 0.0300 MPa @Strain 10.0 % |
4.35 psi @Strain 10.0 % |
BS ISO 7214 1998 |
| 0.0490 MPa @Strain 25.0 % |
7.11 psi @Strain 25.0 % |
BS ISO 7214 1998 | |
| 0.0770 MPa @Strain 40.0 % |
11.2 psi @Strain 40.0 % |
BS ISO 7214 1998 | |
| 0.109 MPa @Strain 50.0 % |
15.8 psi @Strain 50.0 % |
BS ISO 7214 1998 | |
| Tear Strength | 0.535 kN/m | 3.05 pli | BS EN ISO 8067 1995 |
| Compression Set | 4.5 % @Time 79200 sec, Strain 25.0 % |
4.5 % @Time 22.0 hour, Strain 25.0 % |
24 hr recovery; BS ISO 7214 1998 |
| 11.5 % @Time 79200 sec, Strain 25.0 % |
11.5 % @Time 22.0 hour, Strain 25.0 % |
0.5 hr recovery; BS ISO 7214 1998 | |
| 16.5 % @Time 79200 sec, Strain 50.0 % |
16.5 % @Time 22.0 hour, Strain 50.0 % |
24 hr recovery; BS ISO 7214 1998 | |
| 25 % @Time 79200 sec, Strain 50.0 % |
25 % @Time 22.0 hour, Strain 50.0 % |
0.5 hr recovery; BS ISO 7214 1998 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 0.0506 W/m-K | 0.351 BTU-in/hr-ft²-°F | mean temp of 10°C; ISO 8302 1991 |
| Maximum Service Temperature, Air | 100 °C | 212 °F | |
| Minimum Service Temperature, Air | -70.0 °C | -94.0 °F | |
| Flammability Test | 1.5 @Thickness 13.0 mm |
1.5 @Thickness 0.512 in |
Horizontal Burn Rate, mm/sec; ISO 7214 1998 |
| 2.1 @Thickness 5.00 mm |
2.1 @Thickness 0.197 in |
Horizontal Burn Rate, mm/sec; ISO 7214 1998 | |
| Shrinkage | <= 1.0 % @Temperature 70.0 °C, Time 180000 sec |
<= 1.0 % @Temperature 158 °F, Time 50.0 hour |
|
| 1.5 % @Temperature 70.0 °C, Time 1.80e+6 sec |
1.5 % @Temperature 158 °F, Time 500 hour |
||
| 1.8 % @Temperature 80.0 °C, Time 3600 sec |
1.8 % @Temperature 176 °F, Time 1.00 hour |
||
| 4.0 % @Temperature 80.0 °C, Time 180000 sec |
4.0 % @Temperature 176 °F, Time 50.0 hour |
||
| 5.2 % @Temperature 80.0 °C, Time 1.80e+6 sec |
5.2 % @Temperature 176 °F, Time 500 hour |