Zotefoams Plastazote® LD15FM Low Density Polyethylene Foam, Flame Retarded

Category	Polymer , Thermoplastic , Polyethylene (PE) , LDPE
Manufacturer	Zotefoams
Trade Name	Plastazote®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Zotefoams Plastazote® LD15FM Low Density Polyethylene Foam, Flame Retarded.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Plastazote® is a closed cell, cross-linked polyethylene foam manufactured using nitrogen expansion technology to produce foams with exceptional cell size uniformity, low odor / high purity and outstanding physical attributes.Compliant with EC food contact and US FDA regulations.Information provided by Zotefoams

Physical Properties	Metric	English	Comments
Density	0.0150 g/cc	0.000542 lb/in³	Nominal skin/skin; BS ISO 7214 1998
	0.0140 - 0.0190 g/cc	0.000506 - 0.000686 lb/in³	sheet density
Cell Length	0.350 mm	0.0138 in	Typical Diameter
	0.200 - 0.600 mm	0.00787 - 0.0236 in

Mechanical Properties	Metric	English	Comments
Hardness, Shore OO	44	44	10 mm cell/cell thickness; ISO 868 1985
Tensile Strength	0.185 MPa	26.8 psi	ISO 7214 1998
Elongation at Break	95 %	95 %
Compressive Yield Strength	0.0240 MPa @Strain 10.0 %	3.48 psi @Strain 10.0 %	BS ISO 7214 1998
	0.0430 MPa @Strain 25.0 %	6.24 psi @Strain 25.0 %	BS ISO 7214 1998
	0.0730 MPa @Strain 40.0 %	10.6 psi @Strain 40.0 %	BS ISO 7214 1998
	0.104 MPa @Strain 50.0 %	15.1 psi @Strain 50.0 %	BS ISO 7214 1998
Tear Strength	0.305 kN/m	1.74 pli	BS EN ISO 8067 1995
Compression Set	7.5 % @Time 79200 sec, Strain 25.0 %	7.5 % @Time 22.0 hour, Strain 25.0 %	24 hr recovery; BS ISO 7214 1998
	14.5 % @Time 79200 sec, Strain 25.0 %	14.5 % @Time 22.0 hour, Strain 25.0 %	0.5 hr recovery; BS ISO 7214 1998
	24.5 % @Time 79200 sec, Strain 50.0 %	24.5 % @Time 22.0 hour, Strain 50.0 %	24 hr recovery; BS ISO 7214 1998
	31 % @Time 79200 sec, Strain 50.0 %	31 % @Time 22.0 hour, Strain 50.0 %	0.5 hr recovery; BS ISO 7214 1998

Thermal Properties	Metric	English	Comments
Thermal Conductivity	0.0400 W/m-K	0.278 BTU-in/hr-ft²-°F	mean temp of 10°C; ISO 8302 1991
Maximum Service Temperature, Air	95.0 °C	203 °F
Minimum Service Temperature, Air	-70.0 °C	-94.0 °F

Descriptive Properties	Value	Comments
Flammability	Automotive: FMVSS.302 burn rate	Pass: 2 mm and thicker
	Construction: DIN4102 pt14-B1	Pass: 6 to 20 mm thick
	Horizontal Burn Rate: ISO 7214 1998	Extinguishes and melts from flame

Users viewing this material also viewed the following: