Zotefoams Plastazote® HD80 High Density Polyethylene Foam

Category Polymer , Thermoplastic , Polyethylene (PE)
Manufacturer Zotefoams
Trade Name Plastazote®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Zotefoams Plastazote® HD80 High Density Polyethylene Foam.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Plastazote® is a closed cell, cross-linked polyethylene foam manufactured using nitrogen expansion technology to produce foams with exceptional cell size uniformity, low odor / high purity and outstanding physical attributes.Compliant with EC food contact and US FDA regulations.Information provided by Zotefoams
Physical Properties Metric English Comments
Density 0.0580 - 0.0870 g/cc
0.00210 - 0.00314 lb/in³
sheet density
0.0800 g/cc
0.00289 lb/in³
Nominal skin/skin; BS ISO 7214 1998
Cell Length 0.600 mm
0.0236 in
Typical Diameter
0.400 - 0.850 mm
0.0157 - 0.0335 in
Mechanical Properties Metric English Comments
Hardness, Shore OO 81
81
10 mm cell/cell thickness; ISO 868 1985
Tensile Strength 2.09 MPa
303 psi
ISO 7214 1998
Elongation at Break 115 %
115 %
Flexural Modulus 0.0150 GPa
2.18 ksi
BS4370, part 4, method 14
Compressive Yield Strength 0.426 MPa

@Strain 10.0 %
61.8 psi

@Strain 10.0 %
BS ISO 7214 1998
0.523 MPa

@Strain 25.0 %
75.9 psi

@Strain 25.0 %
BS ISO 7214 1998
0.530 MPa

@Strain 40.0 %
76.9 psi

@Strain 40.0 %
BS ISO 7214 1998
0.593 MPa

@Strain 50.0 %
86.0 psi

@Strain 50.0 %
BS ISO 7214 1998
Tear Strength 4.97 kN/m
28.4 pli
BS EN ISO 8067 1995
Compression Set 7.0 %

@Time 79200 sec,
Strain 25.0 %
7.0 %

@Time 22.0 hour,
Strain 25.0 %
24 hr recovery; BS ISO 7214 1998
12 %

@Time 79200 sec,
Strain 50.0 %
12 %

@Time 22.0 hour,
Strain 50.0 %
24 hr recovery; BS ISO 7214 1998
13 %

@Time 79200 sec,
Strain 25.0 %
13 %

@Time 22.0 hour,
Strain 25.0 %
0.5 hr recovery; BS ISO 7214 1998
21.5 %

@Time 79200 sec,
Strain 50.0 %
21.5 %

@Time 22.0 hour,
Strain 50.0 %
0.5 hr recovery; BS ISO 7214 1998
Thermal Properties Metric English Comments
Thermal Conductivity 0.0630 W/m-K
0.437 BTU-in/hr-ft²-°F
mean temp of 10°C; ISO 8302 1991
Maximum Service Temperature, Air 130 °C
266 °F
Minimum Service Temperature, Air -70.0 °C
-94.0 °F
Flammability Test 0.40

@Thickness 13.0 mm
0.40

@Thickness 0.512 in
Horizontal Burn Rate, mm/sec; ISO 7214 1998
0.60

@Thickness 5.00 mm
0.60

@Thickness 0.197 in
Horizontal Burn Rate, mm/sec; ISO 7214 1998