Zotefoams Plastazote® HD60 High Density Polyethylene Foam

Category Polymer , Thermoplastic , Polyethylene (PE)
Manufacturer Zotefoams
Trade Name Plastazote®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Zotefoams Plastazote® HD60 High Density Polyethylene Foam.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Plastazote® is a closed cell, cross-linked polyethylene foam manufactured using nitrogen expansion technology to produce foams with exceptional cell size uniformity, low odor / high purity and outstanding physical attributes.Compliant with EC food contact and US FDA regulations.Information provided by Zotefoams
Physical Properties Metric English Comments
Density 0.0430 - 0.0630 g/cc
0.00155 - 0.00228 lb/in³
sheet density
0.0600 g/cc
0.00217 lb/in³
Nominal skin/skin; BS ISO 7214 1998
Cell Length 0.600 mm
0.0236 in
Typical Diameter
0.400 - 0.850 mm
0.0157 - 0.0335 in
Mechanical Properties Metric English Comments
Hardness, Shore OO 78
78
10 mm cell/cell thickness; ISO 868 1985
Tensile Strength 1.72 MPa
249 psi
ISO 7214 1998
Elongation at Break 110 %
110 %
Flexural Modulus 0.0110 GPa
1.60 ksi
BS4370, part 4, method 14
Compressive Yield Strength 0.296 MPa

@Strain 10.0 %
42.9 psi

@Strain 10.0 %
BS ISO 7214 1998
0.326 MPa

@Strain 25.0 %
47.3 psi

@Strain 25.0 %
BS ISO 7214 1998
0.345 MPa

@Strain 40.0 %
50.0 psi

@Strain 40.0 %
BS ISO 7214 1998
0.398 MPa

@Strain 50.0 %
57.7 psi

@Strain 50.0 %
BS ISO 7214 1998
Tear Strength 3.525 kN/m
20.11 pli
BS EN ISO 8067 1995
Compression Set 7.0 %

@Time 79200 sec,
Strain 25.0 %
7.0 %

@Time 22.0 hour,
Strain 25.0 %
24 hr recovery; BS ISO 7214 1998
12 %

@Time 79200 sec,
Strain 50.0 %
12 %

@Time 22.0 hour,
Strain 50.0 %
24 hr recovery; BS ISO 7214 1998
12.5 %

@Time 79200 sec,
Strain 25.0 %
12.5 %

@Time 22.0 hour,
Strain 25.0 %
0.5 hr recovery; BS ISO 7214 1998
21 %

@Time 79200 sec,
Strain 50.0 %
21 %

@Time 22.0 hour,
Strain 50.0 %
0.5 hr recovery; BS ISO 7214 1998
Thermal Properties Metric English Comments
Thermal Conductivity 0.0572 W/m-K
0.397 BTU-in/hr-ft²-°F
mean temp of 10°C; ISO 8302 1991
Maximum Service Temperature, Air 125 °C
257 °F
Minimum Service Temperature, Air -70.0 °C
-94.0 °F
Flammability Test 0.60

@Thickness 13.0 mm
0.60

@Thickness 0.512 in
Horizontal Burn Rate, mm/sec; ISO 7214 1998
0.80

@Thickness 5.00 mm
0.80

@Thickness 0.197 in
Horizontal Burn Rate, mm/sec; ISO 7214 1998