Zotefoams Plastazote® HD30 High Density Polyethylene Foam

Category Polymer , Thermoplastic , Polyethylene (PE)
Manufacturer Zotefoams
Trade Name Plastazote®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Zotefoams Plastazote® HD30 High Density Polyethylene Foam.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Plastazote® is a closed cell, cross-linked polyethylene foam manufactured using nitrogen expansion technology to produce foams with exceptional cell size uniformity, low odor / high purity and outstanding physical attributes.Compliant with EC food contact and US FDA regulations.Information provided by Zotefoams
Physical Properties Metric English Comments
Density 0.0230 - 0.0330 g/cc
0.000831 - 0.00119 lb/in³
sheet density
0.0300 g/cc
0.00108 lb/in³
Nominal skin/skin; BS ISO 7214 1998
Cell Length 0.400 mm
0.0157 in
Typical Diameter
0.250 - 0.700 mm
0.00984 - 0.0276 in
Mechanical Properties Metric English Comments
Hardness, Shore OO 73
73
10 mm cell/cell thickness; ISO 868 1985
Tensile Strength 1.01 MPa
146 psi
ISO 7214 1998
Elongation at Break 70 %
70 %
Flexural Modulus 0.00360 GPa
0.522 ksi
BS4370, part 4, method 14
Compressive Yield Strength 0.131 MPa

@Strain 10.0 %
19.0 psi

@Strain 10.0 %
BS ISO 7214 1998
0.158 MPa

@Strain 25.0 %
22.9 psi

@Strain 25.0 %
BS ISO 7214 1998
0.184 MPa

@Strain 40.0 %
26.7 psi

@Strain 40.0 %
BS ISO 7214 1998
0.222 MPa

@Strain 50.0 %
32.2 psi

@Strain 50.0 %
BS ISO 7214 1998
Tear Strength 1.415 kN/m
8.074 pli
BS EN ISO 8067 1995
Compression Set 6.0 %

@Time 79200 sec,
Strain 25.0 %
6.0 %

@Time 22.0 hour,
Strain 25.0 %
24 hr recovery; BS ISO 7214 1998
11 %

@Time 79200 sec,
Strain 25.0 %
11 %

@Time 22.0 hour,
Strain 25.0 %
0.5 hr recovery; BS ISO 7214 1998
15 %

@Time 79200 sec,
Strain 50.0 %
15 %

@Time 22.0 hour,
Strain 50.0 %
24 hr recovery; BS ISO 7214 1998
22.5 %

@Time 79200 sec,
Strain 50.0 %
22.5 %

@Time 22.0 hour,
Strain 50.0 %
0.5 hr recovery; BS ISO 7214 1998
Thermal Properties Metric English Comments
Thermal Conductivity 0.0471 W/m-K
0.327 BTU-in/hr-ft²-°F
mean temp of 10°C; ISO 8302 1991
Maximum Service Temperature, Air 120 °C
248 °F
Minimum Service Temperature, Air -70.0 °C
-94.0 °F
Flammability Test 1.8

@Thickness 13.0 mm
1.8

@Thickness 0.512 in
Horizontal Burn Rate, mm/sec; ISO 7214 1998
2.5

@Thickness 5.00 mm
2.5

@Thickness 0.197 in
Horizontal Burn Rate, mm/sec; ISO 7214 1998