Zotefoams Evazote® VA25 Ethylene Vinyl Acetate Copolymer Foam

Category	Polymer , Thermoplastic , Ethylene Vinyl Acetate
Manufacturer	Zotefoams
Trade Name	Evazote®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Zotefoams Evazote® VA25 Ethylene Vinyl Acetate Copolymer Foam.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Evazote® is a closed cell, cross-linked EVA copolymer foam manufactured using nitrogen expansion technology to produce foams with exceptional cell size uniformity, low odor / high purity and outstanding physical attributes.Compliant with EC food contact and US FDA regulations.Information provided by Zotefoams

Physical Properties	Metric	English	Comments
Density	0.0200 - 0.0280 g/cc	0.000723 - 0.00101 lb/in³	sheet density
	0.0250 g/cc	0.000903 lb/in³	Nominal skin/skin; BS ISO 7214 1998
Cell Length	0.200 - 0.600 mm	0.00787 - 0.0236 in
	0.400 mm	0.0157 in	Typical Diameter

Mechanical Properties	Metric	English	Comments
Hardness, Shore OO	43	43	10 mm cell/cell thickness; ISO 868 1985
Tensile Strength	0.485 MPa	70.3 psi	ISO 7214 1998
Elongation at Break	150 %	150 %
Compressive Yield Strength	0.0220 MPa @Strain 10.0 %	3.19 psi @Strain 10.0 %	BS ISO 7214 1998
	0.0410 MPa @Strain 25.0 %	5.95 psi @Strain 25.0 %	BS ISO 7214 1998
	0.0700 MPa @Strain 40.0 %	10.2 psi @Strain 40.0 %	BS ISO 7214 1998
	0.100 MPa @Strain 50.0 %	14.5 psi @Strain 50.0 %	BS ISO 7214 1998
Tear Strength	0.420 kN/m	2.40 pli	BS EN ISO 8067 1995
Compression Set	5.0 % @Time 79200 sec, Strain 25.0 %	5.0 % @Time 22.0 hour, Strain 25.0 %	24 hr recovery; BS ISO 7214 1998
	13 % @Time 79200 sec, Strain 25.0 %	13 % @Time 22.0 hour, Strain 25.0 %	0.5 hr recovery; BS ISO 7214 1998
	19.5 % @Time 79200 sec, Strain 50.0 %	19.5 % @Time 22.0 hour, Strain 50.0 %	24 hr recovery; BS ISO 7214 1998
	29 % @Time 79200 sec, Strain 50.0 %	29 % @Time 22.0 hour, Strain 50.0 %	0.5 hr recovery; BS ISO 7214 1998

Thermal Properties	Metric	English	Comments
Thermal Conductivity	0.0374 W/m-K	0.260 BTU-in/hr-ft²-°F	mean temp of 10°C; ISO 8302 1991
Maximum Service Temperature, Air	75.0 °C	167 °F
Minimum Service Temperature, Air	-70.0 °C	-94.0 °F
Flammability Test	1.9 @Thickness 13.0 mm	1.9 @Thickness 0.512 in	Horizontal Burn Rate, mm/sec; ISO 7214 1998
	3.6 @Thickness 5.00 mm	3.6 @Thickness 0.197 in	Horizontal Burn Rate, mm/sec; ISO 7214 1998

Descriptive Properties	Value	Comments
Flammability	Automotive: FMVSS.302 burn rate	Pass: 4mm and thicker