Zotefoams Evazote® EV70CN Conductive Ethylene Vinyl Acetate Copolymer Foam

Category Polymer , Thermoplastic , Ethylene Vinyl Acetate
Manufacturer Zotefoams
Trade Name Evazote®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Zotefoams Evazote® EV70CN Conductive Ethylene Vinyl Acetate Copolymer Foam.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Evazote® is a closed cell, cross-linked EVA copolymer foam manufactured using nitrogen expansion technology to produce foams with exceptional cell size uniformity, low odor / high purity and outstanding physical attributes.Information provided by Zotefoams
Physical Properties Metric English Comments
Density 0.0700 g/cc
0.00253 lb/in³
Nominal skin/skin; BS ISO 7214 1998
0.0610 - 0.0810 g/cc
0.00220 - 0.00293 lb/in³
sheet density
Cell Length 0.600 mm
0.0236 in
Typical Diameter
0.400 - 0.900 mm
0.0157 - 0.0354 in
Mechanical Properties Metric English Comments
Hardness, Shore OO 64
64
10 mm cell/cell thickness; ISO 868 1985
Tensile Strength 0.850 MPa
123 psi
ISO 7214 1998
Elongation at Break 225 %
225 %
Compressive Yield Strength 0.0830 MPa

@Strain 10.0 %
12.0 psi

@Strain 10.0 %
BS ISO 7214 1998
0.107 MPa

@Strain 25.0 %
15.5 psi

@Strain 25.0 %
BS ISO 7214 1998
0.143 MPa

@Strain 40.0 %
20.7 psi

@Strain 40.0 %
BS ISO 7214 1998
0.184 MPa

@Strain 50.0 %
26.7 psi

@Strain 50.0 %
BS ISO 7214 1998
Tear Strength 2.75 kN/m
15.7 pli
BS EN ISO 8067 1995
Compression Set 2.5 %

@Time 79200 sec,
Strain 25.0 %
2.5 %

@Time 22.0 hour,
Strain 25.0 %
24 hr recovery; BS ISO 7214 1998
6.0 %

@Time 79200 sec,
Strain 25.0 %
6.0 %

@Time 22.0 hour,
Strain 25.0 %
0.5 hr recovery; BS ISO 7214 1998
8.5 %

@Time 79200 sec,
Strain 50.0 %
8.5 %

@Time 22.0 hour,
Strain 50.0 %
24 hr recovery; BS ISO 7214 1998
17 %

@Time 79200 sec,
Strain 50.0 %
17 %

@Time 22.0 hour,
Strain 50.0 %
0.5 hr recovery; BS ISO 7214 1998
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 80.0 °C
176 °F
Minimum Service Temperature, Air -70.0 °C
-94.0 °F
Flammability Test 0.50

@Thickness 13.0 mm
0.50

@Thickness 0.512 in
Horizontal Burn Rate, mm/sec; ISO 7214 1998
0.70

@Thickness 5.00 mm
0.70

@Thickness 0.197 in
Horizontal Burn Rate, mm/sec; ISO 7214 1998
Electrical Properties Metric English Comments
Volume Resistivity 1000 ohm-cm
1000 ohm-cm
ASTM D991-89
Descriptive Properties Value Comments
Flammability Automotive: FMVSS.302 burn rate
Pass: 3mm and thicker