Zircar Refractory Composites RS-C ALUMINA-SILICA MOLDABLE

Category	Ceramic , Oxide , Aluminum Oxide , Silicon Oxide
Manufacturer	Zircar Refractory Composites, Inc.
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Zircar Refractory Composites RS-C ALUMINA-SILICA MOLDABLE.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

ZIRCAR Alumina-Silica Insulating Blanket Type RS-C Moldable is composed of long, high strength ceramic fibers, with an inorganic alumina binder/rigidizing agent. It is a wet blanket that is shipped rolled up and sealed in a plastic bag to preserve its moldability.Information provided by ZIRCAR Refractory Composites, Inc. (ZRCI)

Physical Properties	Metric	English	Comments
Density	0.460 g/cc	0.0166 lb/in³

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	0.480 MPa	69.6 psi
Compressive Yield Strength	0.200 MPa	29.0 psi	at 10% Compression

Thermal Properties	Metric	English	Comments
Thermal Conductivity	0.0600 W/m-K @Temperature 200 °C	0.416 BTU-in/hr-ft²-°F @Temperature 392 °F	ASTM C177
	0.130 W/m-K @Temperature 500 °C	0.902 BTU-in/hr-ft²-°F @Temperature 932 °F	ASTM C177
	0.200 W/m-K @Temperature 800 °C	1.39 BTU-in/hr-ft²-°F @Temperature 1470 °F	ASTM C177
Maximum Service Temperature, Air	1260 °C	2300 °F
Shrinkage	0.000 % @Temperature 75.0 °C	0.000 % @Temperature 167 °F	Drying
	2.00 % @Temperature 800 °C, Time 86400 sec	2.00 % @Temperature 1470 °F, Time 24.0 hour

Component Elements Properties	Metric	English	Comments
Al2O3	66 %	66 %
SiO2	34 %	34 %

Descriptive Properties	Value	Comments
Color	White