Zircar Ceramics ZAL-15AA Alumina Insulation
| Category | Ceramic , Oxide , Aluminum Oxide |
| Manufacturer | Zircar Ceramics |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Zircar Ceramics ZAL-15AA Alumina Insulation.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
ZAL-15 is a low thermal conductivity uniformly bound fiber board. It is ideal for machining into precision thermal insulators.Information provided by Zircar Ceramics.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.240 g/cc | 0.00867 lb/in³ | |
| Open Porosity | 93 % | 93 % |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Strength | 6.55 MPa @Strain 15.0 % |
950 psi @Strain 15.0 % |
Load applied normal to fiber plane, strain = load deformation in mils; Three Point Bending, Sample 0.5"*0.5"*4" |
| 6.55 MPa @Strain 7.00 % |
950 psi @Strain 7.00 % |
Load applied parallel to fiber plane, strain = load deformation in mils; Three Point Bending, Sample 0.5"*0.5"*4" | |
| Compressive Yield Strength | 0.0689 MPa @Strain 3.00 % |
10.0 psi @Strain 3.00 % |
Load applied normal to fiber plane |
| 0.103 MPa @Strain 5.00 % |
15.0 psi @Strain 5.00 % |
Load applied normal to fiber plane | |
| 0.172 MPa @Strain 3.00 % |
25.0 psi @Strain 3.00 % |
Load applied parallel to fiber plane | |
| 0.345 MPa @Strain 8.00 % |
50.0 psi @Strain 8.00 % |
Load applied parallel to fiber plane |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 7.50 µm/m-°C @Temperature 20.0 - 1000 °C |
4.17 µin/in-°F @Temperature 68.0 - 1830 °F |
|
| Specific Heat Capacity | 1.05 J/g-°C | 0.250 BTU/lb-°F | |
| Thermal Conductivity | 0.0600 W/m-K @Temperature 250 °C |
0.416 BTU-in/hr-ft²-°F @Temperature 482 °F |
parallel to thickness; ASTM C177-76 |
| 0.0800 W/m-K @Temperature 525 °C |
0.555 BTU-in/hr-ft²-°F @Temperature 977 °F |
Parallel to Thickness; ASTM C177-76 | |
| 0.120 W/m-K @Temperature 800 °C |
0.833 BTU-in/hr-ft²-°F @Temperature 1470 °F |
Parallel to Thickness; ASTM C177-76 | |
| 0.160 W/m-K @Temperature 1075 °C |
1.11 BTU-in/hr-ft²-°F @Temperature 1967 °F |
Parallel to Thickness; ASTM C177-76 | |
| 0.220 W/m-K @Temperature 1250 °C |
1.53 BTU-in/hr-ft²-°F @Temperature 2280 °F |
Parallel to Thickness; ASTM C177-76 | |
| 0.250 W/m-K @Temperature 1350 °C |
1.74 BTU-in/hr-ft²-°F @Temperature 2460 °F |
Parallel to Thickness; ASTM C177-76 | |
| Melting Point | 1870 °C | 3400 °F | |
| Maximum Service Temperature, Air | 1500 °C | 2730 °F | Continuous |
| 1600 °C | 2910 °F | Intermittent | |
| Shrinkage | 2.00 % @Temperature 1550 °C, Time 3600 sec |
2.00 % @Temperature 2820 °F, Time 1.00 hour |
Perpendicular to Thickness |
| 6.00 % @Temperature 1650 °C, Time 3600 sec |
6.00 % @Temperature 3000 °F, Time 1.00 hour |
Perpendicular to Thickness |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Al2O3 | 97 % | 97 % | |
| SiO2 | 3.0 % | 3.0 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | White |
Users viewing this material also viewed the following:
- Polykemi AB POLYfill PP CIP1001F Polypropylene
- Supreme Petrochem SP 6460 High Heat Polystyrene
- A. Schulman POLYBATCH™ Buff 60234 Concentrate Based In LDPE
- Zotefoams Plastazote® LD28 Low Density Polyethylene Foam
- ELASTO UK Dryflex® 600700S SEBS Based Material, Filled Qualities, 70A Hardness, Natural
- Dynasol Calprene® 419 Thermoplastic Rubber SBS Dry
- Amity Thermosets ATI 101 Phenolic Molding Organic Filler, Injection Molded
- 3M Scotch-Weld™ 78 HT Hi-Temperature Polystyrene Foam Insulation Cylinder Spray Adhesive
- LATI LASULF G/20 20% Glass Reinforced Polysulfone (PSU) (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved