Zircar Ceramics Z-MAG/2300 Soluble Fiber Insulation

Category	Ceramic , Oxide , Silicon Oxide
Manufacturer	Zircar Ceramics
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Zircar Ceramics Z-MAG/2300 Soluble Fiber Insulation.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

ZIRCAR NON-RCF Insulation Type Z-MAG/2300 is a rigid combination of soluble NON-RCF silica magnesia glass fibers and inorganic binder. It is suitable for use as a substitute for insulation containing refractory ceramic fiber materials in applications with temperatures to 1260°C (2300°F).Information provided by Zircar Ceramics.

Physical Properties	Metric	English	Comments
Density	0.240 g/cc	0.00867 lb/in³
Filament Diameter	4.6 µm	4.6 µm

Mechanical Properties	Metric	English	Comments
Modulus of Rupture	0.000586 GPa	0.0850 ksi	Parallel to Thickness
Compressive Yield Strength	0.0138 MPa	2.00 psi	at 1% Comp., RT, Parallel to Thickness
	0.0172 MPa	2.50 psi	at 2% Comp., RT, Parallel to Thickness

Thermal Properties	Metric	English	Comments
Thermal Conductivity	0.100 W/m-K @Temperature 400 °C	0.694 BTU-in/hr-ft²-°F @Temperature 752 °F	parallel to thickness
	0.220 W/m-K @Temperature 1100 °C	1.53 BTU-in/hr-ft²-°F @Temperature 2010 °F	parallel to thickness
Maximum Service Temperature, Air	1260 °C	2300 °F
Shrinkage	0.300 % @Temperature 870 °C, Time 86400 sec	0.300 % @Temperature 1600 °F, Time 24.0 hour	Length & Width
	0.950 % @Temperature 870 °C, Time 86400 sec	0.950 % @Temperature 1600 °F, Time 24.0 hour	Thickness

Component Elements Properties	Metric	English
CaO	3.75 %	3.75 %
MgO	23 %	23 %
SiO2	77 %	77 %