Zircar Ceramics SALI Alumina Insulation

Category Ceramic , Oxide , Aluminum Oxide
Manufacturer Zircar Ceramics
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Zircar Ceramics SALI Alumina Insulation.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
SALI has been serving 1700°C low mass furnace users longer than any other alumina fiber board available today. SALI is a premium grade rigid fiber board with superior hot strength.Information provided by Zircar Ceramics.
Physical Properties Metric English Comments
Density 0.480 g/cc
0.0173 lb/in³
Open Porosity 84 %
84 %
Mechanical Properties Metric English Comments
Flexural Strength 2.07 MPa
300 psi
Parallel to thickness
Compressive Yield Strength 1.31 MPa
190 psi
at 10% Compression, Parallel to thickness
Thermal Properties Metric English Comments
CTE, linear 8.00 µm/m-°C

@Temperature 20.0 - 1100 °C
4.44 µin/in-°F

@Temperature 68.0 - 2010 °F
Specific Heat Capacity 1.05 J/g-°C
0.250 BTU/lb-°F
Thermal Conductivity 0.200 W/m-K

@Temperature 400 °C
1.39 BTU-in/hr-ft²-°F

@Temperature 752 °F
Parallel to Thickness; ASTM C177-76
0.310 W/m-K

@Temperature 800 °C
2.15 BTU-in/hr-ft²-°F

@Temperature 1470 °F
Parallel to Thickness; ASTM C177-76
0.390 W/m-K

@Temperature 1400 °C
2.71 BTU-in/hr-ft²-°F

@Temperature 2550 °F
Parallel to Thickness; ASTM C177-76
Melting Point 1870 °C
3400 °F
Maximum Service Temperature, Air 1700 °C
3090 °F
Softening Point 1100 °C
2010 °F
Temperature sample yields under load of push rod in CTE determination
Shrinkage 2.00 %
2.00 %
SAG/Distortion, 6in. (152mm) x 1in. (25.4mm) x 1in. (25.4mm), 5in. (127mm) Span, % after 24 hrs. at 1650°C
1.00 %

@Temperature 1650 °C,
Time 86400 sec
1.00 %

@Temperature 3000 °F,
Time 24.0 hour
Perpendicular to Thickness
3.00 %

@Temperature 1700 °C,
Time 86400 sec
3.00 %

@Temperature 3090 °F,
Time 24.0 hour
Perpendicular to Thickness
Component Elements Properties Metric English Comments
Al2O3 80 %
80 %
SiO2 20 %
20 %
Descriptive Properties Value Comments
Bond Silica
Color White