Zell-Metall Engineering Plastics Zellamid 1100 OIL

Category Polymer , Thermoplastic , Nylon , Nylon 6
Manufacturer Zell-Metall Engineering Plastics
Trade Name Zellamid
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Zell-Metall Engineering Plastics Zellamid 1100 OIL.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Zellamid® 1100 OIL: A new type of cast nylon produced by addition of a special oil to the polymer structure. By laboratory test it was proven that this second generation oil filled product reduces friction in comparison to standard cast nylon.This means that Zellamid® 1100 OIL is particularly well suited for sliding parts under high load and increased speed.The specific advantages of Zellamid® 1100 OIL against Zellamid® 1100 are as follows:High degree of self lubrication.Low static coefficient of friction.Low dynamic coefficient of friction.Reduced heat build-up.Better wear and enormously increased part life due to less heat build-up in the area of friction.Reduced moisture absorption (about 5% for Zellamid® 1100 OIL vs. 6-7% for Zellamid® 1100).Increased dimensional stability.Zellamid® 1100 OIL features a homogeneous distribution of the lubricating oil during polymerization. Therefore the improved sliding properties remain, even after machining and part wear. The p. v. value may be used as a guideline to determine the loading capacity of slide bearings at a certain velocity. The values mentioned in the attached data sheet apply for the material combination of Zellamid® and metal for continuous use when heat is well conducted and environmental temperature is normal. Higher are permissible when on is intermittent.When using additional lubricants with Zellamid® 1100 OIL, the external lubricant influences the coefficient of friction to a very high degree. It can be reduced to 0.05. Consequently, the p. v. value may be increased. The advantages of the integrated lubrication of Zellamid® 1100 OIL are particularly noticeable when there is a combination of static and dynamic friction, especially when external lubrication is insufficient or imposible. Zellamid® 1100 OIL is supplied in yellow colour for easy identification.
Physical Properties Metric English Comments
Density 1.14 g/cc
0.0412 lb/in³
Moisture Absorption at Equilibrium 2.0 - 2.5 %
2.0 - 2.5 %
Saturation at 50% RH
Water Absorption at Saturation 4.0 - 5.0 %
4.0 - 5.0 %
23°C
Mechanical Properties Metric English Comments
Hardness, Shore D 80 - 82
80 - 82
DIN 53505
Ball Indentation Hardness 135 MPa
19600 psi
DIN 53456
Tensile Strength at Break 64.0 - 66.0 MPa
9280 - 9570 psi
DIN 53455
Elongation at Break 40 - 60 %
40 - 60 %
DIN 53455
Tensile Modulus 3.20 GPa
464 ksi
DIN 53457
0.700 GPa

@Temperature 100 °C
102 ksi

@Temperature 212 °F
DIN 53457
Charpy Impact Unnotched NB
NB
DIN 53453
Charpy Impact, Notched 8.00 - 10.0 J/cm²
38.1 - 47.6 ft-lb/in²
DIN 53453
Coefficient of Friction 0.050 - 0.10
0.050 - 0.10
to steel, added lubrication
0.15 - 0.29
0.15 - 0.29
to steel, no lubrication; ISO/DTR 7147
Abrasion 55
55
mm³; DIN 53516
Thermal Properties Metric English Comments
CTE, linear 80.0 µm/m-°C

@Temperature 20.0 °C
44.4 µin/in-°F

@Temperature 68.0 °F
Specific Heat Capacity 1.67 J/g-°C
0.399 BTU/lb-°F
Thermal Conductivity 0.280 W/m-K
1.94 BTU-in/hr-ft²-°F
DIN 52612
Melting Point 205 °C
401 °F
Maximum Service Temperature, Air 100 - 120 °C
212 - 248 °F
long time operation
120 - 140 °C
248 - 284 °F
medium time operation
160 °C
320 °F
a few hours operation
Minimum Service Temperature, Air -40.0 °C
-40.0 °F
Descriptive Properties Value Comments
Permissible Unit Pressure 18 - 23 MPa
Time yield limit up to 4
s1/1000; DIN.53444