Wolf Kunststoff ZEDEX® ZX-324VMT A3B PEEK, Fiber Reinforced

Category	Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, PTFE-Filled
Manufacturer	Wolf Kunststoff
Trade Name	ZEDEX®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Wolf Kunststoff ZEDEX® ZX-324VMT A3B PEEK, Fiber Reinforced.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Main Characteristics: Maximum rigidity; Very good wear resistance; Low stick-slip tendency; Stress resistantApplications: Shipbuilding; Chemical Engineering; Automitve Technology; Machine ToolsInformation provided by Zedex

Physical Properties	Metric	English	Comments
Density	1.48 g/cc	0.0535 lb/in³	ISO 1183
Water Absorption	0.050 % @Temperature 23.0 °C	0.050 % @Temperature 73.4 °F	RMC 93%; DIN EN ISO 62
Moisture Absorption at Equilibrium	0.10 %	0.10 %	DIN EN ISO 62

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	>= 100	>= 100	DIN 53505
Hardness, Shore D	88	88	DIN 53505
Ball Indentation Hardness	231 MPa	33500 psi	DIN 2039
Tensile Strength at Break	2.70 MPa	392 psi	DIN EN ISO 527
Tensile Strength	142 MPa	20600 psi	DIN EN ISO 527
Tensile Stress	44.0 MPa @Strain 1.00 %, Time 3.60e+6 sec	6380 psi @Strain 1.00 %, Time 1000 hour	DIN 53444
Tensile Strength, Yield	64.0 MPa	9280 psi	Elastic Limit
	120 MPa	17400 psi	DIN EN ISO 527
Elongation at Break	4.5 %	4.5 %
	4.5 %	4.5 %	DIN EN ISO 527
Elongation at Yield	3.9 %	3.9 %	Elongation at Maximum Force; DIN EN ISO 527
Tensile Modulus	7.80 GPa	1130 ksi	DIN EN ISO 527
Flexural Strength	150 MPa	21800 psi	Outer Fiber Stress at 3.5% Outer Fiber Strain; DIN EN ISO 178
	210 MPa	30500 psi	DIN EN ISO 178
Flexural Modulus	7.00 GPa	1020 ksi	DIN EN ISO 178
Compressive Strength	123 MPa	17800 psi	Elastic Limit
	60.0 MPa @Time 3.60e+7 sec	8700 psi @Time 10000 hour
	109 MPa @Time 360000 sec	15800 psi @Time 100 hour
	131 MPa @Time 36.0 sec	19000 psi @Time 0.0100 hour
	95.0 MPa @Strain 3.50 %	13800 psi @Strain 3.50 %	DIN EN ISO 604
Compressive Modulus	5.454 GPa	791.0 ksi	DIN EN ISO 604
Fatigue Strength	105 MPa @# of Cycles 1.00e+6	15200 psi @# of Cycles 1.00e+6	1 Hz
K Factor (ISO)	0.40 µm/km @Temperature 20.0 °C	0.40 µm/km @Temperature 68.0 °F
	1.8 µm/km @Temperature 100 °C	1.8 µm/km @Temperature 212 °F
	3.6 µm/km @Temperature 200 °C	3.6 µm/km @Temperature 392 °F
	5.2 µm/km @Temperature 240 °C	5.2 µm/km @Temperature 464 °F
Charpy Impact Unnotched	2.30 J/cm²	10.9 ft-lb/in²	EN ISO 179/1eU
Charpy Impact, Notched	0.930 J/cm²	4.43 ft-lb/in²	EN ISO 179/1eA
Coefficient of Friction, Dynamic	0.080 @Temperature 100 °C	0.080 @Temperature 212 °F	Dry Operation
	0.10 @Temperature 20.0 °C	0.10 @Temperature 68.0 °F	Dry Operation
Coefficient of Friction, Static	0.12 @Temperature 20.0 °C	0.12 @Temperature 68.0 °F	Dry Operation
Tensile Creep Modulus, 1000 hours	4560 MPa	661000 psi	At 1% Deformation; DIN 53444
Limiting Pressure Velocity	0.250 MPa-m/sec	7140 psi-ft/min	v = 1m/min
	0.350 MPa-m/sec	9990 psi-ft/min	v = 100m/min
	0.46667 MPa-m/sec	13323 psi-ft/min	v = 200m/min
	0.635 MPa-m/sec	18100 psi-ft/min	v = 10m/min
Compression Set	4.8 %	4.8 %	Elastic Compression Limit

Thermal Properties	Metric	English	Comments
CTE, linear	35.0 µm/m-°C @Temperature <=100 °C	19.4 µin/in-°F @Temperature <=212 °F	ISO E 830
	38.0 µm/m-°C @Temperature <=150 °C	21.1 µin/in-°F @Temperature <=302 °F	ISO E 831
Specific Heat Capacity	1.06 J/g-°C	0.253 BTU/lb-°F	DSC
Thermal Conductivity	0.240 W/m-K	1.67 BTU-in/hr-ft²-°F	DIN 52612
Melting Point	340 °C	644 °F	DSC
Maximum Service Temperature, Air	140 °C	284 °F	Pressed Bushings
	250 °C	482 °F	Continuous
	260 °C	500 °F	Short Term (3h)
Deflection Temperature at 1.8 MPa (264 psi)	270 °C	518 °F	DIN EN ISO 75
Glass Transition Temp, Tg	146 °C	295 °F	DSC
Flammability, UL94	V-0	V-0
Oxygen Index	43 %	43 %	DIN EN ISO 4589

Electrical Properties	Metric	English	Comments
Volume Resistivity	30000 ohm-cm	30000 ohm-cm	IEC 93
Surface Resistance	19000 ohm	19000 ohm	IEC 93
Dielectric Constant	3.3 @Frequency 110 Hz	3.3 @Frequency 110 Hz	IEC 250
Dielectric Strength	0.100 kV/mm	2.54 kV/in	IEC 243
Dissipation Factor	0.0040	0.0040	IEC 112
	0.061 @Frequency 1.00 Hz	0.061 @Frequency 1.00 Hz

Descriptive Properties	Value	Comments
Alignment Adjustment	1	Nominal Scale: 1, low; 10, high
Chemical Sterilization	10	Nominal Scale: 1, low; 10, high
Color	Anthracite
Creep Resistance	7	Nominal Scale: 1, low; 10, high
Dimensional Stability with Thermal Expansion	7	Nominal Scale: 1, low; 10, high
Free from Silicon	Applicable
Gamma-rays Radiation Sterilization	7	Nominal Scale: 1, low; 10, high
Injection Molded Parts	Applicable
Machined Parts	Applicable
Moist Heat Sterilization	7	Nominal Scale: 1, low; 10, high
Plastic Granules	Applicable
Resistance Against dust, Dirt, Abrasive Substances	10	Nominal Scale: 1, low; 10, high
Resistance Against Hot Water	200
Resistance to Chemicals	8	Nominal Scale: 1, low; 10, high
Resistant Against Disinfectant	Applicable
Rods up to Øe (de)	Applicable
ROHS/WEEE	Applicable
Sheets up to Maximum Thickness	Applicable
Sliding Velocity	100
Suitable for Outdoor Use	6	Nominal Scale: 1, low; 10, high
Suitable for Use in Water	Applicable
Suitable for Vacuum	Applicable
Tubes (hollow rods) up to Øe (de)	Applicable
UV Rays Resistance	9	Nominal Scale: 1, low; 10, high
UV-Sterilization	10	Nominal Scale: 1, low; 10, high