Westlake Plastics PEEK Film Made from VICTREX® Polymer

Category Polymer , Film , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, Unreinforced
Manufacturer Westlake Plastics
Trade Name PEEK
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Westlake Plastics PEEK Film Made from VICTREX® Polymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Extremely high temperature resistance and continuous use temperature. Excellent flexural and tensile properties. Good abrasion and rain erosion resistance. Excellent chemical resistance. Excellent electrical properties. Information provided by Westlake Plastics.
Physical Properties Metric English Comments
Density 1.256 g/cc
0.04538 lb/in³
ASTM D792
Water Absorption 0.40 %
0.40 %
ASTM D570; 24 hrs.
Mechanical Properties Metric English Comments
Tensile Strength at Break 120 MPa
17400 psi
ASTM D882
Elongation at Break 50 %
50 %
ASTM D882
Tensile Modulus 2.699 GPa
391.5 ksi
ASTM D882
Flexural Modulus 3.66 GPa
531 ksi
ASTM D790
Tear Strength 13.7 kN/m
78.4 pli
ASTM D1004
Thermal Properties Metric English Comments
Melting Point 340 °C
644 °F
DSC
Maximum Service Temperature, Air 240 °C
464 °F
Continuous Use
Deflection Temperature at 1.8 MPa (264 psi) 166 °C
330 °F
ASTM D648
Glass Transition Temp, Tg 142.7 °C
288.9 °F
ASTM D3418
Flammability, UL94 V-0
V-0
VTM-1
NBS Smoke Density <= 1.0
<= 1.0
ASTM E662
Oxygen Index 23 %
23 %
ASTM D2863
Optical Properties Metric English Comments
Haze 0.50 %
0.50 %
ASTM D1003
Electrical Properties Metric English Comments
Surface Resistance 1.80e+15 ohm
1.80e+15 ohm
ASTM D257
Dielectric Constant 3.3

@Frequency 1000 Hz
3.3

@Frequency 1000 Hz
ASTM D150
Dielectric Strength 126 kV/mm

@Thickness 0.0762 mm
3200 kV/in

@Thickness 0.00300 in
ASTM D149
Dissipation Factor 0.0026

@Frequency 10000 Hz
0.0026

@Frequency 10000 Hz
ASTM D150