Westlake Plastics Absylux® FR Acrylonitrile-Butadiene-Styrene Flame Retardant

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant
Manufacturer Westlake Plastics
Trade Name Absylux®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Westlake Plastics Absylux® FR Acrylonitrile-Butadiene-Styrene Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Absylux ABS is a low cost engineering plastic that is easy to machine and fabricate. It is an ideal material for structural applications when impact resistance, strength, and stiffness are required. Absylux is widely used for machining preproduction prototypes since it has excellent dimensional stability and is easy to paint and glue. This is also available in flame retardant grade. Information provided by Westlake Plastics.
Physical Properties Metric English Comments
Density 1.22 g/cc
0.0441 lb/in³
ASTM D792
Mechanical Properties Metric English Comments
Hardness, Rockwell R 97
97
ASTM D7852
Tensile Strength, Yield 37.9 MPa
5500 psi
ASTM D638
Tensile Modulus 2.21 GPa
320 ksi
ASTM D638
Flexural Yield Strength 65.5 MPa
9500 psi
ASTM D790
Flexural Modulus 2.28 GPa
330 ksi
ASTM D790
Compressive Strength 52.7 MPa
7650 psi
ASTM D695
Compressive Modulus 1.38 GPa
200 ksi
ASTM D695
Izod Impact, Notched 2.14 J/cm
4.00 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
CTE, linear 73.8 µm/m-°C

@Temperature 20.0 °C
41.0 µin/in-°F

@Temperature 68.0 °F
ASTM E831
Deflection Temperature at 0.46 MPa (66 psi) 90.6 °C
195 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 78.3 °C
173 °F
ASTM D648
Flammability, UL94 V-0

@Thickness 1.47 mm
V-0

@Thickness 0.0580 in
Electrical Properties Metric English Comments
Dielectric Strength 40.0 kV/mm
1020 kV/in
ASTM D149