Westlake EB171 MDPE Medium Density Polyethylene

Category	Polymer , Thermoplastic , Polyethylene (PE) , LDPE
Manufacturer	Westlake Chemical Corporation
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Westlake EB171 MDPE Medium Density Polyethylene.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Westlake EF171 is a MDPE resin suggested for use in shrink packaging applications. This material has good TD shrinkage, good optical properties, excellent machinability, and toughness. This resin grade complies with 21 CFR 177.1520. Melt temperatures of 380ï¿½ F ï¿½ 410ï¿½ F are recommended for Westlake Chemical EB171 with blow-up ratios of 2.0:1 or higher. It is Kosher compliant. Test specimens for blown film: nominal thickness 1.3 mils; blow up ratio 2.5:1, die gap 50 mils. Resin contains low slip, low antiblock.

Physical Properties	Metric	English	Comments
Density	0.930 g/cc	0.0336 lb/in³	ASTM-D1505
Thickness	33.0 microns	1.30 mil
Melt Flow	1.6 g/10 min	1.6 g/10 min	ASTM-D1238

Mechanical Properties	Metric	English	Comments
Film Elongation at Break, MD	300 %	300 %	ASTM-D882
Film Elongation at Break, TD	800 %	800 %	ASTM-D882
Dart Drop	<= 2.56 g/micron	<= 65.0 g/mil	ASTM-D1709
Film Tensile Strength at Break, MD	26.2 MPa	3800 psi	ASTM-D882
Film Tensile Strength at Break, TD	18.6 MPa	2700 psi	ASTM-D882
1% Secant Modulus, MD	338 MPa	49000 psi	ASTM-D882
1% Secant Modulus, TD	448 MPa	65000 psi	ASTM-D882

Processing Properties	Metric	English	Comments
Melt Temperature	193 - 210 °C	380 - 410 °F
Blow-up Ratio (BUR)	2.5	2.5