Wellman Wellamid® FRGF25-66-N Flame Retardant Nylon 66, Lubricated, 25% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass Fiber Filled, Flame Retardant |
| Manufacturer | Wellman Engineering Resins |
| Trade Name | Wellamid® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Wellman Wellamid® FRGF25-66-N Flame Retardant Nylon 66, Lubricated, 25% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Typical Applications: Electrical terminal blocks, electric fan switch housings, coil forms, multi-pin electrical connectors, electric fan switch housings, TV tuner components, automotive switch housings.Data provided by the manufacturer, Wellman Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | ISO 1183 |
| Water Absorption | 1.4 % | 1.4 % | Approximate 24 hr. |
| Linear Mold Shrinkage | 0.0030 - 0.0070 cm/cm | 0.0030 - 0.0070 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 110 MPa | 16000 psi | ISO 527 |
| Elongation at Break | 2.0 % | 2.0 % | ISO 527 |
| Flexural Yield Strength | 165 MPa | 23900 psi | ISO 178 |
| Flexural Modulus | 6.70 GPa | 972 ksi | ISO 178 |
| Izod Impact, Notched | 0.400 J/cm | 0.749 ft-lb/in | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 240 °C | 464 °F | ISO 75 |
| Flammability, UL94 | V-0 @Thickness 0.790 mm |
V-0 @Thickness 0.0311 in |
UL 94 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 271 - 282 °C | 520 - 540 °F | |
| Middle Barrel Temperature | 266 - 277 °C | 510 - 530 °F | |
| Front Barrel Temperature | 260 - 271 °C | 500 - 520 °F | |
| Nozzle Temperature | 271 - 282 °C | 520 - 540 °F | |
| Melt Temperature | 266 - 277 °C | 510 - 530 °F | |
| Mold Temperature | 71.1 - 93.3 °C | 160 - 200 °F | |
| Drying Temperature | 79.4 °C | 175 °F | Opened bags and gaylord boxes |
| Dry Time | 2 - 4 hour | 2 - 4 hour | Opened bags and gaylord boxes |
| Moisture Content | 0.050 - 0.20 % | 0.050 - 0.20 % | During molding to prevent hydrolytic degradation |
| <= 0.20 % | <= 0.20 % | In shipping bags, ready to mold | |
| Injection Pressure | 34.5 - 138 MPa | 5000 - 20000 psi | |
| Back Pressure | 0.345 MPa | 50.0 psi | |
| Screw Speed | 30 - 120 rpm | 30 - 120 rpm |