- Wellman Wellamid® FRGF1850-N1 Nylon 66, 25% Glass Fiber Reinforced, Flame Retardant
Wellman Wellamid® FRGF1850-N1 Nylon 66, 25% Glass Fiber Reinforced, Flame Retardant
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass Fiber Filled, Flame Retardant |
| Manufacturer | Wellman Engineering Resins |
| Trade Name | Wellamid® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Wellman Wellamid® FRGF1850-N1 Nylon 66, 25% Glass Fiber Reinforced, Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
All information provided by Wellman Engineered Resins.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.61 g/cc | 0.0582 lb/in³ | ISO 1183-87 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0070 cm/cm | 0.0030 - 0.0070 in/in | DIS 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.011 cm/cm | 0.0070 - 0.011 in/in | DIS 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 125 MPa | 18100 psi | ISO 527-93 |
| Elongation at Break | 1.5 % | 1.5 % | ISO 527-93 |
| Flexural Strength | 185 MPa | 26800 psi | ISO 178-93 |
| Flexural Modulus | 9.90 GPa | 1440 ksi | ISO 178-93 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | ISO 180-93 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 260 °C | 500 °F | ISO 3146 |
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | ISO 75-93 |
| Flammability, UL94 | V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |