- Wellman EcoLon® MR1660-BK 40% Mineral Reinforced Post Consumer Compound Nylon 66
Wellman EcoLon® MR1660-BK 40% Mineral Reinforced Post Consumer Compound Nylon 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Mineral Filled |
| Manufacturer | Wellman Engineering Resins |
| Trade Name | EcoLon® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Wellman EcoLon® MR1660-BK 40% Mineral Reinforced Post Consumer Compound Nylon 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Mineral Reinforced Post Consumer Compound Nylon 66Information provided by Wellman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.49 g/cc | 0.0538 lb/in³ | ISO 1183-87 |
| Filler Content | 40 % | 40 % | |
| Linear Mold Shrinkage, Flow | 0.0060 - 0.010 cm/cm | 0.0060 - 0.010 in/in | ISO DIS 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0090 - 0.013 cm/cm | 0.0090 - 0.013 in/in | ISO DIS 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 72.0 MPa | 10400 psi | ISO 527-93 |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527-93 |
| Flexural Strength | 125 MPa | 18100 psi | ISO 178-93 |
| Flexural Modulus | 7.00 GPa | 1020 ksi | ISO 178-93 |
| Izod Impact, Notched (ISO) | 3.50 kJ/m² | 1.67 ft-lb/in² | ISO 180-93 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 260 °C | 500 °F | ISO 3146 |
| Deflection Temperature at 1.8 MPa (264 psi) | 170 °C | 338 °F | ISO 75-93 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 282 - 304 °C | 540 - 580 °F | |
| Middle Barrel Temperature | 277 - 299 °C | 530 - 570 °F | |
| Front Barrel Temperature | 271 - 293 °C | 520 - 560 °F | |
| Nozzle Temperature | 282 - 293 °C | 540 - 560 °F | |
| Melt Temperature | 288 - 310 °C | 550 - 590 °F | |
| Mold Temperature | 71.1 - 93.3 °C | 160 - 200 °F | |
| Drying Temperature | 79.4 °C | 175 °F | Opened bags and gaylord boxes |
| Dry Time | 2 - 4 hour | 2 - 4 hour | Opened bags and gaylord boxes |
| Moisture Content | 0.050 - 0.20 % | 0.050 - 0.20 % | During molding to prevent hydrolytic degradation |
| <= 0.20 % | <= 0.20 % | In shipping bags, ready to mold | |
| Injection Pressure | 34.5 - 138 MPa | 5000 - 20000 psi | |
| Back Pressure | 0.345 MPa | 50.0 psi | |
| Screw Speed | 30 - 120 rpm | 30 - 120 rpm |
Users viewing this material also viewed the following:
- Polikim KESTAMID® GRF Polyamide 6, Graphite Filled
- Eastman 1924P Polyethylene (discontinued **)
- TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, 400ºF Cure Temperature
- PolyOne Geon™ Vinyl Flexible R353AE Polyvinyl Chloride, Flexible (PVC, Flexible)
- H.C. Starck Amperit® 518.001 Agglomerated, Sintered Tungsten Carbide-Cobalt 88-12 (WC-CO)
- Johnson Matthey Mattibraze 50 Cadmium Containing Silver Brazing Alloy
- Zyvex Performance Materials Aroply™ 350 Nano-Engineered Composite Film Adhesive
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 0.25 PHR Thanecure ZM
Copyright © lookpolymers.com All Rights Reserved