Wanhua Chemical Wanthane® WHT-1585 Polyester Based TPU
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyurethane TPE , Polyurethane, TP , Thermoplastic Polyurethane (TPUR), Polyester Grade |
| Manufacturer | Wanhua Chemical Group Co., Ltd. |
| Trade Name | Wanthane® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Wanhua Chemical Wanthane® WHT-1585 Polyester Based TPU.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Low cost, good mechanical properties, good processabilityInformation provided by Wanhua Chemical Group Co., Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 86 | 86 | ASTM D2240 |
| Tensile Strength | 30.0 MPa | 4350 psi | ASTM D412 |
| Elongation at Break | 630 % | 630 % | ASTM D412 |
| 100% Modulus | 0.00600 GPa | 0.870 ksi | ASTM D412 |
| 300% Modulus | 0.0300 GPa | 4.35 ksi | ASTM D412 |
| Tear Strength | 90.0 kN/m | 514 pli | ASTM D624 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 185 - 205 °C | 365 - 401 °F |
Users viewing this material also viewed the following:
- Lucite International Elvacite ® 2010 Acrylic Resin
- SABIC Innovative Plastics LNP LUBRICOMP KL001 Acetal Copolymer (Asia Pacific)
- SABIC Innovative Plastics LNP STAT-KON RX98063 PA 66 (Europe-Africa-Middle East)
- Sichuan Deyang Haton® hGR302 PPS / F4 Polyphenylene Sulfide
- Styrolution NOVODUR® P2HGV ABS, 16% Glass Fiber
- Borealis CC7209 Polyethylene
- Dow Corning SILASTIC® T-4 RTV SILICONE RUBBER BASE & CURING AGENT
- Fainplast Compounds EVAtech 807I Ethylene Vinyl Acetate Foam
- DuPont Teijin Films Mylar® D804 Polyester Film, 60 Gauge
Copyright © lookpolymers.com All Rights Reserved