Wanhua Chemical Wanthane® WHT-1180 Polyester Based TPU
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyurethane TPE , Polyurethane, TP , Thermoplastic Polyurethane (TPUR), Polyester Grade |
| Manufacturer | Wanhua Chemical Group Co., Ltd. |
| Trade Name | Wanthane® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Wanhua Chemical Wanthane® WHT-1180 Polyester Based TPU.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Excellent mechanical properties, high abrasion resistance, tear resistance, short cycle timeInformation provided by Wanhua Chemical Group Co., Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in³ | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 80 | 80 | ASTM D2240 |
| Tensile Strength | 30.0 MPa | 4350 psi | ASTM D412 |
| Elongation at Break | 590 % | 590 % | ASTM D412 |
| 100% Modulus | 0.00500 GPa | 0.725 ksi | ASTM D412 |
| 300% Modulus | 0.00900 GPa | 1.31 ksi | ASTM D412 |
| Tear Strength | 87.0 kN/m | 496 pli | ASTM D624 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Glass Transition Temp, Tg | -40.0 °C | -40.0 °F | ASTM D3418 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 180 - 200 °C | 356 - 392 °F |
Users viewing this material also viewed the following:
- Polymer Resources PC-G15 Polycarbonate, 15% Glass Reinforced
- Fainplast Compounds RE 330 Rigid PVC, Extrusion
- SSAB Tunnplat Dogal F26 Metal-coated Mild Steel
- ExxonMobil Bicor™ 25MB666 OPP Film
- 3M 9925XL Extended Liner Tapes
- Arlon 51808R011 0.011" (0.279 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- Plaskolite West Optix® CA - 900 High Impact Acrylic Resin
Copyright © lookpolymers.com All Rights Reserved