Vyncolit X620/1 Novolac Phenolic

Category	Polymer , Thermoset , Filled/Reinforced Thermoset , Phenolic , Phenolic, Novolac, Glass Filled
Manufacturer	Vyncolit N.V., Sumitomo Bakelite
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Vyncolit X620/1 Novolac Phenolic.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Glass fiber and graphite filled phenolic molding compound with excellent friction properties.USES: Low friction bearings, video recorder and compact disc parts. Not suitable for applications requiring electrical insulation.Information provided by Vyncolit, a Sumitomo Bak Group

Physical Properties	Metric	English	Comments
Bulk Density	0.750 g/cc	0.0271 lb/in³	Powder Density; ISO 60
Density	1.67 g/cc	0.0603 lb/in³	Relative Density; ISO 1183
Linear Mold Shrinkage	0.0022 cm/cm	0.0022 in/in	Injection Molding; ISO 2577

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	90.0 MPa	13100 psi	ISO 527
Elongation at Break	0.70 %	0.70 %	Tensile; ISO 527
	1.0 %	1.0 %	Flexure; ISO 178
Tensile Modulus	17.0 GPa	2470 ksi	ISO 527
Flexural Strength	130 MPa	18900 psi	At Rupture; ISO 178
Flexural Modulus	15.0 GPa	2180 ksi	ISO 178
Compressive Strength	170 MPa	24700 psi	ISO 604
Charpy Impact Unnotched	0.700 J/cm²	3.33 ft-lb/in²	ISO 179
Charpy Impact, Notched	0.300 J/cm²	1.43 ft-lb/in²	ISO 179

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	20.0 µm/m-°C @Temperature 20.0 °C	11.1 µin/in-°F @Temperature 68.0 °F	TMA
CTE, linear, Transverse to Flow	35.0 µm/m-°C @Temperature 20.0 °C	19.4 µin/in-°F @Temperature 68.0 °F	TMA
Deflection Temperature at 1.8 MPa (264 psi)	200 °C	392 °F	ISO 75 Af
Flammability, UL94	V-0 @Thickness 1.60 mm	V-0 @Thickness 0.0630 in
	V-0 @Thickness 4.00 mm	V-0 @Thickness 0.157 in
Shrinkage	0.010 %	0.010 %	Post Shrinkage; ISO 2577

Descriptive Properties	Value	Comments
Color	Black
ISO type	PF 2 C1
Main Filler	Glass Fiber & Graphite
Molding Method	Compression, transfer, injection