Vyncolit Neopreg Kinel® SK4525 S5 Glass Fiber Reinforced Molding Compound

Category Polymer , Thermoset , Epoxy , Epoxy Molding Compound , Filled/Reinforced Thermoset
Manufacturer Vyncolit N.V., Sumitomo Bakelite
Trade Name Neopreg Kinel®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Vyncolit Neopreg Kinel® SK4525 S5 Glass Fiber Reinforced Molding Compound.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
BMI molding compound long glass fiber reinforced with excellent mechanical and thermal properties. Especially suited to be used for injection molding.Information provided by Sumitomo Bak North America, Inc.
Physical Properties Metric English Comments
Bulk Density 0.590 g/cc
0.0213 lb/in³
ISO 60
Density 1.66 g/cc
0.0600 lb/in³
ISO 1183
Water Absorption 0.26 %
0.26 %
ISO 62
Linear Mold Shrinkage 0.0015 cm/cm
0.0015 in/in
ISO 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break 80.0 MPa

@Temperature 250 °C
11600 psi

@Temperature 482 °F
ISO 527-1
98.0 MPa

@Temperature 150 °C
14200 psi

@Temperature 302 °F
ISO 527-1
130 MPa

@Temperature 23.0 °C
18900 psi

@Temperature 73.4 °F
ISO 527-1
Elongation at Break 0.60 %

@Temperature 23.0 °C
0.60 %

@Temperature 73.4 °F
ISO 527-1
0.60 %

@Temperature 150 °C
0.60 %

@Temperature 302 °F
ISO 527-1
0.70 %

@Temperature 250 °C
0.70 %

@Temperature 482 °F
ISO 527-1
Tensile Modulus 14.0 GPa

@Temperature 250 °C
2030 ksi

@Temperature 482 °F
ISO 527-1
18.0 GPa

@Temperature 150 °C
2610 ksi

@Temperature 302 °F
ISO 527-1
28.0 GPa

@Temperature 23.0 °C
4060 ksi

@Temperature 73.4 °F
ISO 527-1
Flexural Strength 135 MPa

@Temperature 250 °C
19600 psi

@Temperature 482 °F
ISO 178
287 MPa

@Temperature 150 °C
41600 psi

@Temperature 302 °F
ISO 178
325 MPa

@Temperature 23.0 °C
47100 psi

@Temperature 73.4 °F
ISO 178
Flexural Modulus 13.0 GPa

@Temperature 250 °C
1890 ksi

@Temperature 482 °F
ISO 178
23.0 GPa

@Temperature 150 °C
3340 ksi

@Temperature 302 °F
ISO 178
26.0 GPa

@Temperature 23.0 °C
3770 ksi

@Temperature 73.4 °F
ISO 178
Compressive Strength 127 MPa

@Temperature 250 °C
18400 psi

@Temperature 482 °F
ISO 604
219 MPa

@Temperature 150 °C
31800 psi

@Temperature 302 °F
ISO 604
306 MPa

@Temperature 23.0 °C
44400 psi

@Temperature 73.4 °F
ISO 604
Charpy Impact, Notched 5.20 J/cm²
24.7 ft-lb/in²
ISO 179-1
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 11.0 µm/m-°C
6.11 µin/in-°F
TMA
CTE, linear, Transverse to Flow 45.0 µm/m-°C
25.0 µin/in-°F
TMA
Glass Transition Temp, Tg 275 °C
527 °F
Shrinkage 0.00 %
0.00 %
Post Shrinkage; ISO 2577
Electrical Properties Metric English Comments
Comparative Tracking Index 275 V
275 V
IEC 60250
Descriptive Properties Value Comments
Color Dark Grey
Molding Method Injection