- Victrex® PEEK 90GL30 Polyetheretherketone, 30% Glass Fiber Reinforced
Victrex® PEEK 90GL30 Polyetheretherketone, 30% Glass Fiber Reinforced
| Category | Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, Glass Fiber Filled |
| Manufacturer | Victrex |
| Trade Name | PEEK |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Victrex® PEEK 90GL30 Polyetheretherketone, 30% Glass Fiber Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Description:High performance thermoplastic material, 30% glass fibre reinforced Polyetheretherketone (PEEK), semi crystalline, granules for injection moulding, very easy flow, FDA food contact compliant, colour natural/beige.Typical Application Areas:Complex geometries with thinner cross sections or longer flow lengths where higher strength in a static system is required. Low coefficient of thermal expansion. Chemically resistant to aggressive environments, suitable for sterilization for medical and food contact applications.Information Provided by VICTREX®
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.52 g/cc | 0.0549 lb/in³ | Crystalline; ISO 1183 |
| Water Absorption at Saturation | 0.30 % @Temperature 23.0 °C |
0.30 % @Temperature 73.4 °F |
Equilibrium; by immersion; ISO 62-1 |
| 0.45 % @Temperature 100 °C |
0.45 % @Temperature 212 °F |
immersion; ISO 62-1 | |
| Viscosity | 200000 cP @Temperature 400 °C |
200000 cP @Temperature 752 °F |
melt; ISO 11443 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | 360°C nozzle, 160°C tool; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm | 0.0090 in/in | 370°C nozzle, 180°C tool; ISO 294-4 |
| Spiral Flow | 18.5 cm @Thickness 1.00 mm |
7.28 in @Thickness 0.0394 in |
370°C nozzle, 180°C tool |
| 22.0 cm @Thickness 1.00 mm |
8.66 in @Thickness 0.0394 in |
400°C nozzle, 200°C tool |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 90 @Temperature 23.0 °C |
90 @Temperature 73.4 °F |
ISO 868 |
| Tensile Strength at Break | 45.0 MPa @Temperature 275 °C |
6530 psi @Temperature 527 °F |
ISO 527 |
| 60.0 MPa @Temperature 225 °C |
8700 psi @Temperature 437 °F |
ISO 527 | |
| 80.0 MPa @Temperature 175 °C |
11600 psi @Temperature 347 °F |
ISO 527 | |
| 130 MPa @Temperature 125 °C |
18900 psi @Temperature 257 °F |
ISO 527 | |
| 195 MPa @Temperature 23.0 °C |
28300 psi @Temperature 73.4 °F |
ISO 527 | |
| Elongation at Break | 2.4 % @Temperature 23.0 °C |
2.4 % @Temperature 73.4 °F |
ISO 527 |
| Tensile Modulus | 12.0 GPa @Temperature 23.0 °C |
1740 ksi @Temperature 73.4 °F |
ISO 527 |
| Flexural Strength | 75.0 MPa @Temperature 275 °C |
10900 psi @Temperature 527 °F |
ISO 178 |
| 115 MPa @Temperature 175 °C |
16700 psi @Temperature 347 °F |
ISO 178 | |
| 230 MPa @Temperature 125 °C |
33400 psi @Temperature 257 °F |
ISO 178 | |
| 290 MPa @Temperature 23.0 °C |
42100 psi @Temperature 73.4 °F |
ISO 178 | |
| Flexural Modulus | 11.5 GPa @Temperature 23.0 °C |
1670 ksi @Temperature 73.4 °F |
ISO 178 |
| Compressive Strength | 55.0 MPa @Temperature 250 °C |
7980 psi @Temperature 482 °F |
ISO 604 |
| 160 MPa @Temperature 120 °C |
23200 psi @Temperature 248 °F |
ISO 604 | |
| 250 MPa @Temperature 23.0 °C |
36300 psi @Temperature 73.4 °F |
ISO 604 | |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² @Temperature 23.0 °C |
4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 180/A |
| Izod Impact, Unnotched (ISO) | 45.0 kJ/m² @Temperature 23.0 °C |
21.4 ft-lb/in² @Temperature 73.4 °F |
ISO 180/U |
| Charpy Impact Unnotched | 4.50 J/cm² @Temperature 23.0 °C |
21.4 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1U |
| Charpy Impact, Notched | 0.750 J/cm² @Temperature 23.0 °C |
3.57 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 45.0 µm/m-°C @Temperature <=143 °C |
25.0 µin/in-°F @Temperature <=289 °F |
Average below Tg; ISO 11359 |
| 110 µm/m-°C @Temperature >=143 °C |
61.1 µin/in-°F @Temperature >=289 °F |
Average above Tg; ISO 11359 | |
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C @Temperature <=143 °C |
11.1 µin/in-°F @Temperature <=289 °F |
Below Tg; ISO 11359 |
| 20.0 µm/m-°C @Temperature >=143 °C |
11.1 µin/in-°F @Temperature >=289 °F |
Above Tg; ISO 11359 | |
| Thermal Conductivity | 0.300 W/m-K @Temperature 23.0 °C |
2.08 BTU-in/hr-ft²-°F @Temperature 73.4 °F |
Average; ISO/CD 22007-4 |
| 0.350 W/m-K @Temperature 23.0 °C |
2.43 BTU-in/hr-ft²-°F @Temperature 73.4 °F |
Along flow; ISO 22007-4 | |
| Melting Point | 343 °C | 649 °F | ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 335 °C | 635 °F | ISO 75A-f |
| Glass Transition Temp, Tg | 143 °C | 289 °F | Onset; ISO 11357 |
| Glow Wire Test | 960 °C @Thickness 2.00 mm |
1760 °F @Thickness 0.0787 in |
IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | IEC 60093 |
| Dielectric Constant | 3.3 @Frequency 1000 Hz, Temperature 23.0 °C |
3.3 @Frequency 1000 Hz, Temperature 73.4 °F |
IEC 60250 |
| Dielectric Strength | 23.0 kV/mm @Thickness 2.50 mm |
584 kV/in @Thickness 0.0984 in |
IEC 60243-1 |
| Dissipation Factor | 0.0040 @Frequency 1.00e+6 Hz, Temperature 23.0 °C |
0.0040 @Frequency 1.00e+6 Hz, Temperature 73.4 °F |
IEC 60250 |
| Comparative Tracking Index | 150 V | 150 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | <= 100 °C | <= 212 °F | Hopper Temperature |
| Nozzle Temperature | 370 °C | 698 °F | |
| Mold Temperature | 170 - 200 °C | 338 - 392 °F | |
| Drying Temperature | 120 °C @Time 18000 sec |
248 °F @Time 5.00 hour |
|
| 150 °C @Time 10800 sec |
302 °F @Time 3.00 hour |