- Victrex® PEEK 450CA30 30% Carbon Fiber Reinforced
Victrex® PEEK 450CA30 30% Carbon Fiber Reinforced
| Category | Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, Carbon Fiber Filled |
| Manufacturer | Victrex |
| Trade Name | PEEK |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Victrex® PEEK 450CA30 30% Carbon Fiber Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
General purpose, 30% carbon fiber reinforced, pelletized grade for injection molding.Information provided by Victrex.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | ASTM D792 |
| Water Absorption at Saturation | 0.30 % @Temperature 23.0 °C |
0.30 % @Temperature 73.4 °F |
immersion; ISO 62-1 |
| 0.45 % @Temperature 100 °C |
0.45 % @Temperature 212 °F |
immersion; ISO 62-1 | |
| Viscosity | 675000 cP @Temperature 400 °C |
675000 cP @Temperature 752 °F |
melt; ISO 11443 |
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | 395°C nozzle, 200°C tool; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0050 cm/cm | 0.0050 in/in | 395°C nozzle, 200°C tool; ISO 294-4 |
| Spiral Flow | 7.50 cm @Thickness 1.00 mm |
2.95 in @Thickness 0.0394 in |
395°C nozzle, 200°C tool |
| 33.0 cm @Thickness 3.00 mm |
13.0 in @Thickness 0.118 in |
395°C nozzle, 200°C tool |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 87.5 | 87.5 | ISO 868 |
| Tensile Strength at Break | 50.0 MPa @Temperature 275 °C |
7250 psi @Temperature 527 °F |
ISO 527 |
| 85.0 MPa @Temperature 175 °C |
12300 psi @Temperature 347 °F |
ISO 527 | |
| 160 MPa @Temperature 125 °C |
23200 psi @Temperature 257 °F |
ISO 527 | |
| 265 MPa @Temperature 23.0 °C |
38400 psi @Temperature 73.4 °F |
ISO 527 | |
| Elongation at Break | 1.7 % | 1.7 % | ISO 527 |
| Tensile Modulus | 28.0 GPa | 4060 ksi | ISO 527 |
| Flexural Strength | 65.0 MPa @Temperature 275 °C |
9430 psi @Temperature 527 °F |
ISO 178 |
| 130 MPa @Temperature 175 °C |
18900 psi @Temperature 347 °F |
ISO 178 | |
| 275 MPa @Temperature 125 °C |
39900 psi @Temperature 257 °F |
ISO 178 | |
| 380 MPa @Temperature 23.0 °C |
55100 psi @Temperature 73.4 °F |
ISO 178 | |
| Flexural Modulus | 24.0 GPa | 3480 ksi | ISO 178 |
| Compressive Strength | 70.0 MPa @Temperature 200 °C |
10200 psi @Temperature 392 °F |
ISO 604 |
| 200 MPa @Temperature 120 °C |
29000 psi @Temperature 248 °F |
ISO 604 | |
| 300 MPa @Temperature 23.0 °C |
43500 psi @Temperature 73.4 °F |
ISO 604 | |
| Izod Impact, Notched (ISO) | 10.5 kJ/m² @Temperature 23.0 °C |
5.00 ft-lb/in² @Temperature 73.4 °F |
ISO 180/A |
| Izod Impact, Unnotched (ISO) | 50.0 kJ/m² @Temperature 23.0 °C |
23.8 ft-lb/in² @Temperature 73.4 °F |
ISO 180/U |
| Charpy Impact Unnotched | 4.50 J/cm² @Temperature 23.0 °C |
21.4 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1U |
| Charpy Impact, Notched | 0.700 J/cm² @Temperature 23.0 °C |
3.33 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 40.0 µm/m-°C @Temperature <=143 °C |
22.2 µin/in-°F @Temperature <=289 °F |
Average below Tg; ISO 11359 |
| 100 µm/m-°C @Temperature >=143 °C |
55.6 µin/in-°F @Temperature >=289 °F |
Average above Tg; ISO 11359 | |
| CTE, linear, Parallel to Flow | 5.00 µm/m-°C @Temperature <=143 °C |
2.78 µin/in-°F @Temperature <=289 °F |
Below Tg; ISO 11359 |
| 6.00 µm/m-°C @Temperature >=143 °C |
3.33 µin/in-°F @Temperature >=289 °F |
Above Tg; ISO 11359 | |
| Thermal Conductivity | 0.950 W/m-K | 6.59 BTU-in/hr-ft²-°F | Average; ISO 22007-4 |
| 2.00 W/m-K | 13.9 BTU-in/hr-ft²-°F | Along flow; ISO 22007-4 | |
| Melting Point | 343 °C | 649 °F | ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 336 °C | 637 °F | ISO 75-f |
| Glass Transition Temp, Tg | 143 °C | 289 °F | Onset; ISO 11357 |
| 150 °C | 302 °F | Midpoint; ISO 11357 | |
| UL RTI, Mechanical with Impact | 200 °C | 392 °F | |
| UL RTI, Mechanical without Impact | 240 °C | 464 °F | |
| Glow Wire Test | 960 °C @Thickness 2.00 mm |
1760 °F @Thickness 0.0787 in |
IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1e+05 | 1e+05 | 1V; ASTM D4496 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | <= 100 °C | <= 212 °F | Hopper Temperature |
| Nozzle Temperature | 395 °C | 743 °F | |
| Mold Temperature | 180 - 210 °C | 356 - 410 °F | |
| Dry Time | 2.00 hour @Temperature 120 °C |
2.00 hour @Temperature 248 °F |
|
| 3.00 hour @Temperature 150 °C |
3.00 hour @Temperature 302 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Toxicity Index | 0.05 | CO content |
| 0.12 | CO2 content | |
| 0.17 | Total gases |
Users viewing this material also viewed the following:
- Isoflon PSU Polysulfone
- Lubriplate Super GPO L0752 Heavy-Duty Motor Oil Motor Oil & Transmission Fluid
- Solvay Specialty Polymers Tecnoflon® T 538 Fluoroelastomer
- Styron CALIBREâ„¢ 7101 8 Polycarbonate, 10% Glass Reinforced
- A. Schulman PP 1102-01 Polypropylene General Purpose, Molding Grade Polypropylene
- Total PSI 8350 (AS) High Impact Polystyrene
- Daikin POLYFLON MG-1431F PTFE 20% Glass Fiber and 5% MoS2 Filled Molding Powder, High Apparent Density, Free Flow
- Arkema Group Orgalloy® LT 4060 ES Flexible Nylon Alloy (Conditioned)
- 3M PS191 White Yupo™ TIS Label Products
- Axiall 6300 Rigid PVC, Molding
Copyright © lookpolymers.com All Rights Reserved