Victrex® APTIV® 2000-050 Polyetheretherketone (PEEK) Polymer Film, Amorphous

Category	Polymer , Film , Thermoplastic , Polyketone , Polyetheretherketone (PEEK)
Manufacturer	Victrex
Trade Name	APTIV®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Victrex® APTIV® 2000-050 Polyetheretherketone (PEEK) Polymer Film, Amorphous.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

APTIV PEEK 2000 series films are the unfilled amorphous films made from VICTREX® PEEK polymer. The film provides a material solution for engineers in ultra-high performance applications.APTIV PEEK 2000 has a unique combination of properties providing high temperature performance, light weight, mechanical strength, durability, excellent radiation, hydrolysis and chemical resistance, electrical insulation, wear and abrasion resistance, excellent barrier properties with high purity, good flammability without the use of flame retardants, low toxicity of combustion products, and low moisture absorption in a film format. Inherently halogen free and ease of processing makes APTIV films a technology enabler for our customers and end users.Applications:Aerospace insulationElectrical InsulationAcoustic speaker diaphragmsThermoforming of thin wall partsCompositesAll information provided by Victrex.Properties measured on 50 micron film

Physical Properties	Metric	English	Comments
Specific Gravity	1.26 g/cc @Temperature 23.0 °C	1.26 g/cc @Temperature 73.4 °F	ISO 1183
Moisture Absorption at Equilibrium	0.21 % @Temperature 23.0 °C, Time 86400 sec	0.21 % @Temperature 73.4 °F, Time 24.0 hour	50% RH; ISO 62

Mechanical Properties	Metric	English	Comments
Film Elongation at Break, MD	>= 200 %	>= 200 %	ISO 527
	>= 200 % @Thickness 0.0250 mm	>= 200 % @Thickness 0.000984 in	ISO 527
	>= 200 % @Thickness 0.0250 mm	>= 200 % @Thickness 0.000984 in	ISO 527
Film Elongation at Break, TD	>= 200 %	>= 200 %	ISO 527
	>= 200 % @Thickness 0.100 mm	>= 200 % @Thickness 0.00394 in	ISO 527
	>= 200 % @Thickness 0.100 mm	>= 200 % @Thickness 0.00394 in	ISO 527
Tensile Modulus	1.80 GPa	261 ksi	MD; ISO 527
	1.80 GPa	261 ksi	TD; ISO 527
	1.60 GPa @Thickness 0.100 mm	232 ksi @Thickness 0.00394 in	MD; ISO 527
	1.60 GPa @Thickness 0.100 mm	232 ksi @Thickness 0.00394 in	TD; ISO 527
	1.80 GPa @Thickness 0.0250 mm	261 ksi @Thickness 0.000984 in	MD; ISO 527
	1.80 GPa @Thickness 0.0250 mm	261 ksi @Thickness 0.000984 in	TD; ISO 527
Tear Strength	5.96 kN/m	34.0 pli	MD; ISO 6383-1
	5.96 kN/m	34.0 pli	TD; ISO 6383-1
Film Tensile Strength at Break, MD	120 MPa	17400 psi	ISO 527
	120 MPa @Thickness 0.0250 mm	17400 psi @Thickness 0.000984 in	ISO 527
	130 MPa @Thickness 0.0250 mm	18900 psi @Thickness 0.000984 in	ISO 527
Film Tensile Strength at Break, TD	120 MPa	17400 psi	ISO 527
	120 MPa @Thickness 0.100 mm	17400 psi @Thickness 0.00394 in	ISO 527
	130 MPa @Thickness 0.100 mm	18900 psi @Thickness 0.00394 in	ISO 527

Thermal Properties	Metric	English	Comments
CTE, linear	60.0 µm/m-°C	33.3 µin/in-°F	MD, below Tg; ASTM D696
Shrinkage, MD	<= 10 % @Temperature 200 °C	<= 10 % @Temperature 392 °F	TM-VX-84
Shrinkage, TD	<= 5.0 % @Temperature 200 °C	<= 5.0 % @Temperature 392 °F	TM-VX-84

Electrical Properties	Metric	English	Comments
Volume Resistivity	2.00e+16 ohm-cm @Temperature 23.0 °C	2.00e+16 ohm-cm @Temperature 73.4 °F	100V; ASTM D257
Dielectric Constant	3.3 @Frequency 1e+7 Hz, Temperature 23.0 °C	3.3 @Frequency 1e+7 Hz, Temperature 73.4 °F
Dielectric Strength	190 kV/mm @Temperature 23.0 °C	4830 kV/in @Temperature 73.4 °F	1/4 inch electrode; ASTM D149
	120 kV/mm @Thickness 0.100 mm	3050 kV/in @Thickness 0.00394 in	ASTM D149
	270 kV/mm @Thickness 0.0250 mm	6860 kV/in @Thickness 0.000984 in	ASTM D149
Dielectric Breakdown	6750 V @Thickness 0.0250 mm	6750 V @Thickness 0.000984 in	ASTM D149
	9500 V @Thickness 0.0500 mm	9500 V @Thickness 0.00197 in	ASTM D149
	15000 V @Thickness 0.100 mm	15000 V @Thickness 0.00394 in	ASTM D149
Dissipation Factor	0.0030 @Frequency 1e+7 Hz, Temperature 23.0 °C	0.0030 @Frequency 1e+7 Hz, Temperature 73.4 °F	ASTM D150

Descriptive Properties	Value	Comments
Puncture Strength (kJ/m²)	40	Def Stan 81-75; 23°C