Victrex® APTIV® 1000-050 Polyetheretherketone (PEEK) Polymer Film, Semi-Crystalline

Category Polymer , Film , Thermoplastic , Polyketone , Polyetheretherketone (PEEK)
Manufacturer Victrex
Trade Name APTIV®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Victrex® APTIV® 1000-050 Polyetheretherketone (PEEK) Polymer Film, Semi-Crystalline.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
APTIV PEEK 1000 series films are the unfilled semi-crystalline films made from VICTREX® PEEK polymer. The film provides a material solution for engineers in ultra-high performance applications.APTIV PEEK 1000 has a unique combination of properties providing high temperature performance, light weight, mechanical strength, durability, excellent radiation, hydrolysis and chemical resistance, electrical insulation, wear and abrasion resistance, excellent barrier properties with high purity, good flammability without the use of flame retardants, low toxicity of combustion products, and low moisture absorption in a film format. Inherently halogen free and ease of processing makes APTIV films a technology enabler for our customers and end users.Applications:Electrical insulationPressure sensitive tapesPrinted circuit substratesHigh temperature labelsWashers in high speed motorsWashers in mobile phone hingesFlexible surface heatersAerospace insulationPressure sensor membranesAcoustic speaker diaphragms and voice coilsCapacitorsCompositesProven temperature resistance to use of lead free soldersAll information provided by Victrex.Properties measured on 50 micron film
Physical Properties Metric English Comments
Specific Gravity 1.30 g/cc

@Temperature 23.0 °C
1.30 g/cc

@Temperature 73.4 °F
ISO 1183
Moisture Absorption at Equilibrium 0.040 %

@Temperature 23.0 °C,
Time 86400 sec
0.040 %

@Temperature 73.4 °F,
Time 24.0 hour
50% RH; ISO 62
Mechanical Properties Metric English Comments
Film Elongation at Break, MD >= 150 %
>= 150 %
ISO 527
>= 150 %

@Thickness 0.250 mm
>= 150 %

@Thickness 0.00984 in
ISO 527
>= 150 %

@Thickness 0.125 mm
>= 150 %

@Thickness 0.00492 in
ISO 527
>= 150 %

@Thickness 0.0250 mm
>= 150 %

@Thickness 0.000984 in
ISO 527
Film Elongation at Break, TD >= 150 %
>= 150 %
ISO 527
>= 150 %

@Thickness 0.250 mm
>= 150 %

@Thickness 0.00984 in
ISO 527
>= 150 %

@Thickness 0.125 mm
>= 150 %

@Thickness 0.00492 in
ISO 527
>= 150 %

@Thickness 0.0250 mm
>= 150 %

@Thickness 0.000984 in
ISO 527
Tensile Modulus 2.50 GPa
363 ksi
MD; ISO 527
2.50 GPa
363 ksi
TD; ISO 527
2.30 GPa

@Thickness 0.250 mm
334 ksi

@Thickness 0.00984 in
TD; ISO 527
2.30 GPa

@Thickness 0.250 mm
334 ksi

@Thickness 0.00984 in
MD; ISO 527
2.30 GPa

@Thickness 0.125 mm
334 ksi

@Thickness 0.00492 in
TD; ISO 527
2.30 GPa

@Thickness 0.125 mm
334 ksi

@Thickness 0.00492 in
MD
2.60 GPa

@Thickness 0.0250 mm
377 ksi

@Thickness 0.000984 in
MD; ISO 527
2.80 GPa

@Thickness 0.0250 mm
406 ksi

@Thickness 0.000984 in
TD; ISO 527
Tear Strength 5.96 kN/m
34.0 pli
MD; ISO 6383-1
7.89 kN/m
45.0 pli
TD; ISO 6383-1
Film Tensile Strength at Break, MD 130 MPa
18900 psi
ISO 527
110 MPa

@Thickness 0.250 mm
16000 psi

@Thickness 0.00984 in
ISO 527
120 MPa

@Thickness 0.125 mm
17400 psi

@Thickness 0.00492 in
ISO 527
140 MPa

@Thickness 0.0250 mm
20300 psi

@Thickness 0.000984 in
ISO 527
Film Tensile Strength at Break, TD 120 MPa
17400 psi
ISO 527
110 MPa

@Thickness 0.250 mm
16000 psi

@Thickness 0.00984 in
ISO 527
120 MPa

@Thickness 0.125 mm
17400 psi

@Thickness 0.00492 in
ISO 527
120 MPa

@Thickness 0.0250 mm
17400 psi

@Thickness 0.000984 in
ISO 527
Thermal Properties Metric English Comments
CTE, linear 47.0 µm/m-°C
26.1 µin/in-°F
MD, below Tg; ASTM D696
Thermal Conductivity 0.290 W/m-K
2.01 BTU-in/hr-ft²-°F
Through Plane; ASTM E1461
0.320 W/m-K
2.22 BTU-in/hr-ft²-°F
In-Plane; ASTM E1461
Shrinkage, MD <= 0.50 %

@Temperature 200 °C
<= 0.50 %

@Temperature 392 °F
TM-VX-84
Shrinkage, TD <= 0.50 %

@Temperature 200 °C
<= 0.50 %

@Temperature 392 °F
TM-VX-84
Electrical Properties Metric English Comments
Volume Resistivity 4.00e+16 ohm-cm

@Temperature 23.0 °C
4.00e+16 ohm-cm

@Temperature 73.4 °F
100V; ASTM D257
Dielectric Constant 3.5

@Frequency 1e+7 Hz,
Temperature 23.0 °C
3.5

@Frequency 1e+7 Hz,
Temperature 73.4 °F
Dielectric Strength 190 kV/mm

@Temperature 23.0 °C
4830 kV/in

@Temperature 73.4 °F
1/4 inch electrode; ASTM D149
2.76 kV/mm

@Thickness 0.250 mm
70.0 kV/in

@Thickness 0.00984 in
1/4 inch electrode; ASTM D149
4.72 kV/mm

@Thickness 0.125 mm
120 kV/in

@Thickness 0.00492 in
1/4 inch electrode; ASTM D149
270 kV/mm

@Thickness 0.0250 mm
6860 kV/in

@Thickness 0.000984 in
1/4 inch electrode; ASTM D149
Dielectric Breakdown 6750 V

@Thickness 0.0250 mm
6750 V

@Thickness 0.000984 in
1/4 inch electrode; ASTM D149
9500 V

@Thickness 0.0500 mm
9500 V

@Thickness 0.00197 in
1/4 inch electrode; ASTM D149
15000 V

@Thickness 0.125 mm
15000 V

@Thickness 0.00492 in
1/4 inch electrode; ASTM D149
17500 V

@Thickness 0.250 mm
17500 V

@Thickness 0.00984 in
1/4 inch electrode; ASTM D149
Dissipation Factor 0.0020

@Frequency 1e+7 Hz,
Temperature 23.0 °C
0.0020

@Frequency 1e+7 Hz,
Temperature 73.4 °F
ASTM D150
Descriptive Properties Value Comments
Puncture Strength (kJ/m²) 26
Def Stan 81-75; 23°C