- Vicone High Performance Rubber VicoSil™ 159DLK-RD High Performance Silicone Rubber
Vicone High Performance Rubber VicoSil™ 159DLK-RD High Performance Silicone Rubber
| Category | Polymer , Thermoset , Rubber or Thermoset Elastomer (TSE) , Silicone , Silicone Rubber |
| Manufacturer | Vicone High Performance Rubber |
| Trade Name | VicoSil™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Vicone High Performance Rubber VicoSil™ 159DLK-RD High Performance Silicone Rubber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Meets AMS 3302 Silicone 50 Durometer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.21 g/cc | 0.0437 lb/in³ | ASTM D297 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 52 | 52 | ASTM D2240 |
| Tensile Strength | 7.90 MPa | 1150 psi | ASTM D412 |
| 2.41 MPa @Strain 100 % |
350 psi @Strain 100 % |
ASTM D412 | |
| Elongation at Break | 381 % | 381 % | ASTM D412 |
| Compressive Modulus | 0.00280 GPa @Strain 5 % |
0.406 ksi @Strain 5 % |
ISO-7743 |
| 0.00290 GPa @Strain 10 % |
0.421 ksi @Strain 10 % |
ISO-7743 | |
| 0.00310 GPa @Strain 20 % |
0.450 ksi @Strain 20 % |
ISO-7743 | |
| 0.00330 GPa @Strain 25 % |
0.479 ksi @Strain 25 % |
ISO-7743 | |
| Tear Strength | 6.60 kN/m | 37.7 pli | ASTM D624 |
| Compression Set | 22.8 % @Temperature 150 °C, Time 252000 sec |
22.8 % @Temperature 302 °F, Time 70.0 hour |
ASTM D395 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Brittleness Temperature | <= -65.0 °C | <= -85.0 °F | passes at 3 min.; ASTM D2137 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Red | |
| Effect of Liquids - Change in Elongation (%) | -6.7 | ASTM D471; 150°C; 70 h |
| Effect of Liquids - Change in Hardness (%) | -7 | ASTM D471; 150°C; 70 h |
| Effect of Liquids - Change in Tensile Strength (%) | -5.5 | ASTM D471; 150°C; 70 h |
| Effect of Liquids - Change in Volume after Oil Immersion (%) | 6.9 | ASTM D471; 150°C; 70 h |
| Heat Aging - Change in Elongation (%) | -33.2 | ASTM D573; 225°C; 70h |
| Heat Aging - Change in Hardness (%) | 7 | ASTM D573; 225°C; 70h |
| Heat Aging - Change in Tensile Strength (%) | -16.72 | ASTM D573; 225°C; 70h |
Users viewing this material also viewed the following:
- Polykemi AB POLYelast TPE R44 Thermoplastic Elastomer
- PolyMirae Moplen HP550K Stretch/Yarn, Monofilament Grade Polypropylene
- Industrial Laminates/Norplex P95 Glass Fabric
- Mearthane Durethaneâ„¢ S DS-210A Solid Polyurethane Elastomer
- DuPont Nucrel® 699 Ethylene-Methacrylic Acid Copolymer Resin
- DuPont Teijin Films Mylar® EB31 Polyester Film, 200 Gauge
- Azoty Tarnow™ Alphalon™ 27D Nylon 6
- Asahi Kasei Thermylene® P6-30FG-1734 30% Glass Fiber Reinforced, Heat Stabilized
- Axiall 12870 Wire & Cable Flexible PVC
- ExxonMobil Label-Lyte® 65 LIM-301 White Opaque OPP Film for Injection Mold Label Applications
Copyright © lookpolymers.com All Rights Reserved