Unitika U-8000

Category Polymer , Thermoplastic , Polyarylate
Manufacturer Unitika
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Unitika U-8000.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
U series resins are polymer alloys that are improved in resistance to oils and chemicals, the shortcoming of amorphous resins. They are transparent and have a greater moisture blocking property than other resins having similar structures. They are also suitable for blow molding.Characteristics:Transparent, resistant to chemicals, especially to oils, alcohols and others Weather Resistance Blended into PET resins for improvement in heat resistance.Information provided by Unitika Ltd.
Physical Properties Metric English Comments
Density 1.26 g/cc
0.0455 lb/in³
ASTM D792
Water Absorption 0.15 %

@Thickness 3.17 mm,
Time 86400 sec
0.15 %

@Thickness 0.125 in,
Time 24.0 hour
ASTM D570
Linear Mold Shrinkage, Flow 0.0080 cm/cm

@Thickness 3.00 mm
0.0080 in/in

@Thickness 0.118 in
Mechanical Properties Metric English Comments
Hardness, Rockwell R 125
125
ASTM D785
Tensile Strength at Break 87.0 MPa
12600 psi
ASTM D638
Elongation at Break 105 %
105 %
ASTM D638
Flexural Strength 103 MPa
14900 psi
ASTM D790
Flexural Modulus 2.70 GPa
392 ksi
ASTM D790
Compressive Strength 86.0 MPa
12500 psi
ASTM D695
Izod Impact, Notched 1.08 J/cm

@Thickness 3.17 mm
2.02 ft-lb/in

@Thickness 0.125 in
ASTM D256
Thermal Properties Metric English Comments
CTE, linear 62.0 µm/m-°C
34.4 µin/in-°F
ASTM D696
Deflection Temperature at 1.8 MPa (264 psi) 110 °C
230 °F
ASTM D648
Electrical Properties Metric English Comments
Volume Resistivity 2.00e+14 ohm-cm
2.00e+14 ohm-cm
ASTM D257
Dielectric Constant 3.0

@Frequency 1.00e+6 Hz
3.0

@Frequency 1.00e+6 Hz
ASTM D150
Dielectric Strength 44.1 kV/mm
1120 kV/in
ASTM D149
Dissipation Factor 0.015

@Frequency 1.00e+6 Hz
0.015

@Frequency 1.00e+6 Hz
ASTM D150
Arc Resistance 120 sec
120 sec
ASTM D495
Comparative Tracking Index 232 V
232 V
Processing Properties Metric English Comments
Rear Barrel Temperature 250 - 270 °C
482 - 518 °F
Middle Barrel Temperature 260 - 280 °C
500 - 536 °F
Front Barrel Temperature 270 - 290 °C
518 - 554 °F
Nozzle Temperature 270 - 290 °C
518 - 554 °F
Mold Temperature 70.0 - 90.0 °C
158 - 194 °F
actual surface temp
Drying Temperature 110 °C
230 °F
Dry Time 10.0 - 24.0 hour
10.0 - 24.0 hour
Back Pressure 0.490 - 1.47 MPa
71.1 - 213 psi
gage pressure