Unitika B2040G33 PA66, 33% Glass Fiber Reinforced, Conditioned
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | Unitika |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Unitika B2040G33 PA66, 33% Glass Fiber Reinforced, Conditioned.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Unitika Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.39 g/cc | 0.0502 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 1.7 % | 1.7 % | 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Thickness 3.20 mm |
0.0030 in/in @Thickness 0.126 in |
|
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm @Thickness 3.20 mm |
0.0080 in/in @Thickness 0.126 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 125 MPa | 18100 psi | ISO 527-1/-2 |
| Elongation at Break | 4.0 % | 4.0 % | ISO 527-1/-2 |
| Tensile Modulus | 6.70 GPa | 972 ksi | ISO 527-1/-2 |
| Flexural Strength | 190 MPa | 27600 psi | ISO 178 |
| Flexural Modulus | 6.50 GPa | 943 ksi | ISO 178 |
| Charpy Impact Unnotched | 8.00 J/cm² | 38.1 ft-lb/in² | ISO 179-1 |
| Charpy Impact, Notched | 1.40 J/cm² | 6.66 ft-lb/in² | ISO 179-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 40.0 µm/m-°C | 22.2 µin/in-°F | ISO 11359-2 |