POLYMER SEARCH

Unitika AXG-1500-300 Conditioned

Category	Polymer , Thermoplastic , Polyarylate
Manufacturer	Unitika
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Unitika AXG-1500-300 Conditioned.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Characteristics: Glass-reinforced grades of the AX1500 resin, excellent in heat and chemical resistancesFavorable rigidity and dimensional accuracyInformation provided by Unitika Ltd.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	112 MPa	16200 psi	ASTM D638
Elongation at Break	6.0 %	6.0 %	ASTM D638
Flexural Strength	181 MPa	26300 psi	ASTM D790
Flexural Modulus	6.30 GPa	914 ksi	ASTM D790
Izod Impact, Notched	1.03 J/cm @Thickness 3.17 mm	1.93 ft-lb/in @Thickness 0.125 in	ASTM D256

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+12 ohm-cm	1.00e+12 ohm-cm	ASTM D257
Dielectric Constant	3.6 @Frequency 1.00e+6 Hz	3.6 @Frequency 1.00e+6 Hz	ASTM D150
Dielectric Strength	30.0 kV/mm	762 kV/in	ASTM D149
Dissipation Factor	0.040 @Frequency 1.00e+6 Hz	0.040 @Frequency 1.00e+6 Hz	ASTM D150
Arc Resistance	60 sec	60 sec	ASTM D495

Processing Properties	Metric	English	Comments
Rear Barrel Temperature	210 - 230 °C	410 - 446 °F
Middle Barrel Temperature	240 - 260 °C	464 - 500 °F
Front Barrel Temperature	250 - 270 °C	482 - 518 °F
Nozzle Temperature	250 - 270 °C	482 - 518 °F
Mold Temperature	80.0 - 120 °C	176 - 248 °F	actual surface temp
Drying Temperature	100 °C	212 °F
Dry Time	10.0 - 24.0 hour	10.0 - 24.0 hour
Back Pressure	0.490 - 1.47 MPa	71.1 - 213 psi	gage pressure

Users viewing this material also viewed the following: