Unitika A125 PA66, Dry

Category	Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced
Manufacturer	Unitika
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Unitika A125 PA66, Dry.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Information provided by Unitika Ltd.

Physical Properties	Metric	English	Comments
Density	1.14 g/cc	0.0412 lb/in³	ISO 1183
Moisture Absorption at Equilibrium	2.3 %	2.3 %	50% RH; ISO 62
Linear Mold Shrinkage, Flow	0.016 cm/cm @Thickness 3.20 mm	0.016 in/in @Thickness 0.126 in
Linear Mold Shrinkage, Transverse	0.022 cm/cm @Thickness 3.20 mm	0.022 in/in @Thickness 0.126 in

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	120	120	ISO 2039
Tensile Strength, Yield	82.0 MPa	11900 psi	ISO 527-1/-2
Elongation at Break	30 %	30 %	ISO 527-1/-2
Tensile Modulus	3.00 GPa	435 ksi	ISO 527-1/-2
Flexural Strength	113 MPa	16400 psi	ISO 178
Flexural Modulus	3.00 GPa	435 ksi	ISO 178
Charpy Impact Unnotched	NB	NB	ISO 179-1
Charpy Impact, Notched	0.500 J/cm²	2.38 ft-lb/in²	ISO 179-1

Thermal Properties	Metric	English	Comments
CTE, linear	90.0 µm/m-°C	50.0 µin/in-°F	ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi)	195 °C	383 °F	ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)	70.0 °C	158 °F	ISO 75-1/-2
Flammability, UL94	V-2 @Thickness 0.810 mm	V-2 @Thickness 0.0319 in

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+12 ohm-cm	1.00e+12 ohm-cm	IEC 60093
Dielectric Constant	3.4 @Frequency 1.00e+6 Hz	3.4 @Frequency 1.00e+6 Hz	IEC 60250
Dielectric Strength	32.0 kV/mm @Thickness 1.00 mm	813 kV/in @Thickness 0.0394 in	IEC 60243-1
Dissipation Factor	0.040 @Frequency 1.00e+6 Hz	0.040 @Frequency 1.00e+6 Hz	IEC 60250
Comparative Tracking Index	600 V	600 V	IEC 60112