Unitika A1030JR PA6, Dry
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced |
| Manufacturer | Unitika |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Unitika A1030JR PA6, Dry.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Unitika Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ISO 1183 |
| Water Absorption | 1.8 % @Time 86400 sec |
1.8 % @Time 24.0 hour |
ISO 62 |
| Moisture Absorption at Equilibrium | 2.8 % | 2.8 % | 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0090 cm/cm @Thickness 3.20 mm |
0.0090 in/in @Thickness 0.126 in |
|
| Linear Mold Shrinkage, Transverse | 0.011 cm/cm @Thickness 3.20 mm |
0.011 in/in @Thickness 0.126 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ISO 2039 |
| Tensile Strength, Yield | 82.0 MPa | 11900 psi | ISO 527-1/-2 |
| Elongation at Break | 30 % | 30 % | ISO 527-1/-2 |
| Elongation at Yield | 4.0 % | 4.0 % | ISO 527-1/-2 |
| Tensile Modulus | 2.90 GPa | 421 ksi | ISO 527-1/-2 |
| Flexural Strength | 105 MPa | 15200 psi | ISO 178 |
| Flexural Modulus | 2.80 GPa | 406 ksi | ISO 178 |
| Charpy Impact Unnotched | NB | NB | ISO 179-1 |
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² | ISO 179-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 96.0 µm/m-°C | 53.3 µin/in-°F | ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 170 °C | 338 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 61.0 °C | 142 °F | ISO 75-1/-2 |
| Flammability, UL94 | V-2 @Thickness 0.840 mm |
V-2 @Thickness 0.0331 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 3.00e+13 ohm-cm | 3.00e+13 ohm-cm | IEC 60093 |
| Dielectric Constant | 3.4 @Frequency 1.00e+6 Hz |
3.4 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dielectric Strength | 37.0 kV/mm @Thickness 1.00 mm |
940 kV/in @Thickness 0.0394 in |
IEC 60243-1 |
| Dissipation Factor | 0.020 @Frequency 1.00e+6 Hz |
0.020 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Comparative Tracking Index | >= 600 V | >= 600 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 230 - 250 °C | 446 - 482 °F | |
| Middle Barrel Temperature | 230 - 250 °C | 446 - 482 °F | |
| Front Barrel Temperature | 220 - 230 °C | 428 - 446 °F | |
| Nozzle Temperature | 230 - 250 °C | 446 - 482 °F | |
| Mold Temperature | 70.0 - 80.0 °C | 158 - 176 °F | |
| Back Pressure | 3.00 - 5.00 MPa | 435 - 725 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Primary Pressure | 50-70 MPa | |
| Secondary Pressure | 40-60 MPa |
Users viewing this material also viewed the following:
- Precision Polymer Engineering E80K Ethylene Propylene Rubber
- DuPont Performance Polymers Crastin® SK642FR BK851 PBT (Unverified Data**)
- Polimeri Europa Dutral® CO 059 Ethylene - Propylene
- Solvay TECHNYL® eXten D247 F Nylon 66 & 610
- SABIC Innovative Plastics ULTEM HU1000 PEI (Europe-Africa-Middle East)
- Shakespeare WN-102 diameter 0.5 mm Nylon 66 Monofilament
- Zylog Hipolyene® 8501 T6 B Thermoplastic Polyolefin & PP Compound
- ExxonMobil Exxsol™ DSP 70/90 Dearomatized Fluid
- DuPont Performance Polymers Hytrel® G4078W TPC-ET (Unverified Data**)
- Axiall 6850 Moldings & Extrusions Flexible PVC
Copyright © lookpolymers.com All Rights Reserved