Uniseal BETABRACE™ 85001 Epoxy

Category Polymer , Thermoset , Epoxy
Manufacturer Uniseal
Trade Name BETABRACE™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Uniseal BETABRACE™ 85001 Epoxy.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
BETABRACE™ 85001 is a composite used for reinforcing sheet metal. It is composed of a moderate temperature curing tacky polymer, woven glass fabric, and release paper. BETABRACE™ 85001 provides excellent adhesion to primed metal and also adheres to oily galvanized and cold rolled steel without a primer. BETABRACE™ 85001 can be supplied in many different shapes and thicknesses for specific reinforcement applications.Information provided by Dow
Physical Properties Metric English Comments
Density 0.752 g/cc
0.0272 lb/in³
Polymer Cured Physical Property
Mechanical Properties Metric English Comments
Modulus of Elasticity 1.47 GPa
213 ksi
Polymer Cured Physical Property
Poissons Ratio 0.11
0.11
Polymer Cured Physical Property
Shear Modulus 0.662 GPa
96.0 ksi
Calculated
Thermal Properties Metric English Comments
Flash Point >= 204 °C
>= 400 °F
Processing Properties Metric English Comments
Cure Time 7.00 min

@Temperature 160 °C
0.117 hour

@Temperature 320 °F
30.0 min

@Temperature 130 °C
0.500 hour

@Temperature 266 °F
Descriptive Properties Value Comments
Flexural Reinforcement Force N 29
2mm deflection; 1.3mm thick; After 500 hrs @ 200°F
32
2mm deflection; 1.9mm thick; After 500 hrs @ 200°F
37
2mm deflection; 1.3mm thick; After 14 days @ 190°F
37
2mm deflection; 1.3mm thick; After 500 hrs @ 100°F & 100% RH
38
2mm deflection; 1.3mm thick; Initial
54
2mm deflection; 1.9mm thick; After 500 hrs @ 100°F & 100% RH
57
2mm deflection; 1.9mm thick; Initial
57
2mm deflection; 1.9mm thick; After 14 days @ 190°F
Max Load N 180
1.3mm thick; 21mm max deflection
255
1.9mm thick; 18mm max deflection