UBE UBESTA® 3030U Nylon 12 (After Zinc chloride aq. for 500 hours)

Category Polymer , Thermoplastic , Nylon , Nylon 12
Manufacturer UBE
Trade Name UBESTA®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF UBE UBESTA® 3030U Nylon 12 (After Zinc chloride aq. for 500 hours).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: UBESTA has a strong resistance to chemicals. Under normal conditions, it is not significantly affected by alkalis, alcohols, ethers, ketones, hydrocarbons, lubricating oils, gasoline, cleaning agents, water, seawater and other chemicals. Compared with other types of plastics, UBESTA is particularly resistant to oils, and it displays strong resistance to organic acids and metal chlorides which adversely affect Nylon 12 and Nylon 66Information provided by UBE.
Mechanical Properties Metric English Comments
Tensile Strength at Break 50.4 MPa
7310 psi
100% Ret.
Tensile Strength, Yield 37.0 MPa
5370 psi
88% Ret.
Elongation at Break 96 %
96 %
120% Ret.
Processing Properties Metric English Comments
Processing Temperature 230 °C
446 °F
Flange Temperature for T-Die Cast Film Extrusion
Zone 1 190 °C
374 °F
For T-Die Cast Film Extrusion
230 °C
446 °F
For 8x1 mm Tube Extrusion
Zone 2 210 °C
410 °F
For T-Die Cast Film Extrusion
225 °C
437 °F
For 8x1 mm Tube Extrusion
Zone 3 220 °C
428 °F
For 8x1 mm Tube Extrusion
230 °C
446 °F
For T-Die Cast Film Extrusion
Zone 4 215 °C
419 °F
For 8x1 mm Tube Extrusion
Die Temperature 230 °C
446 °F
For T-Die Cast Film Extrusion
Die Opening 0.0400 cm
0.0157 in
For T-Die Cast Film Extrusion
Roll Temperature 50.0 °C
122 °F
Chill Roll Temperature for T-Die Cast Film Extrusion
Drying Temperature 80.0 °C
176 °F
Option 1
100 °C
212 °F
Option 2
110 °C
230 °F
Option 3
Dry Time 2 - 4 hour
2 - 4 hour
Option 3
4 - 6 hour
4 - 6 hour
Option 2
6 - 8 hour
6 - 8 hour
Option 1
Screw Speed 15 - 76 rpm
15 - 76 rpm
For 8x1 mm Tube Extrusion
Descriptive Properties Value Comments
C/R 3-3.5:1
For 8x1 mm Tube Extrusion
Calibrating Vacuum 100 mbar
For 8x1 mm Tube Extrusion
Calibration 9.95 mm
For 8x1 mm Tube Extrusion
Compression Ratio min 3:1
For 8x1 mm Tube Extrusion
Die Diameter 16 mm
For 8x1 mm Tube Extrusion
Die Width 300 mm
For T-Die Cast Film Extrusion
Extruder Barmag, Screw Diameter = 30 mm
For T-Die Cast Film Extrusion
Extruder Characteristics 65 mm screw diameter
For 8x1 mm Tube Extrusion
Film Thickness 60 microns
For T-Die Cast Film Extrusion
Haul Off Speed 5 m/min
For T-Die Cast Film Extrusion
Haul Speed 10-55 m/min
For 8x1 mm Tube Extrusion
L/D Ratio 25:1
For 8x1 mm Tube Extrusion
Length of Compression Zone 30% of screw length
For 8x1 mm Tube Extrusion
Length of Feeding Zone 30-40% of screw length
For 8x1 mm Tube Extrusion
Length of Metering Zone 30-45% of screw length
For 8x1 mm Tube Extrusion
Mandrel Diameter 12 mm
For 8x1 mm Tube Extrusion
Tensile Work To Break 962 kJ/m2
118% Ret.
Water Temperature 10-18°C
For 8x1 mm Tube Extrusion
Users viewing this material also viewed the following: