- UBE UBEPOL BR15HL HIPS (n-DM = 0.03 wt % and PH-3H = 0.03 wt %)
UBE UBEPOL BR15HL HIPS (n-DM = 0.03 wt % and PH-3H = 0.03 wt %)
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Impact Modified |
| Manufacturer | UBE |
| Trade Name | UBEPOL |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | UBE UBEPOL BR15HL HIPS (n-DM = 0.03 wt % and PH-3H = 0.03 wt %).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: UBEPOL-BR15HL is a linear type of polymer with the high solution viscosity. In case of enlarging the dispersed rubber particle size in
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Particle Size | 1.0 µm | 1.0 µm | Rubber Particle Size |
| Melt Flow | 2.7 g/10 min | 2.7 g/10 min |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 29.0 MPa | 4210 psi | |
| Tensile Strength, Yield | 33.0 MPa | 4790 psi | |
| Elongation at Break | 8.0 % | 8.0 % | |
| Izod Impact, Notched | 0.740 J/cm | 1.39 ft-lb/in |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 101 °C | 214 °F |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Gloss | 83 % | 83 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| MEK/Acetone Insolubles (wt.%) | 24.1 | |
| Swelling Index | 12.6 |